Functional transition metal silicates

ABSTRACT

The present invention provides a functional transition metal silicate (FTMS) effective as a decontaminant, a disinfectant, a detoxificant, a protectant, a microbicide or combination thereof, comprising a ratio of transition metal to silica in the transition metal silicate in a predetermined range and a structural composition for said effectiveness, said FTMS being capable of being immobilized on a suitable materials or incorporating into resins and/or coating along with resins on suitable materials.

FIELD OF THE INVENTION

The present invention in general relates to the field of functional transition metal silicates. In particular, the present invention relates to synthesis of functional transition metal silicates (FTMS) with required structural composition for the targeted activities.

This invention more particularly relates to synthesis of functional transition metal silicates such as silver silicate, cupric silicate, zinc silicate, manganese silicate and zirconium silicate, having structural composition for effective decontamination, disinfection and microbicidal properties.

This invention also relates to immobilization of functional transition metal silicates (such as silver silicate, cupric silicate, zinc silicate, manganese silicate and zirconium silicate) on activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, incorporating into resins and functional transition metal silicate containing resin coating on solid matrix like quartz sand for effective decontamination, disinfection, microbicidal and toxic gas detoxification properties.

These functional transition metal silicates are useful as decontaminants (by sequestering metals, chemicals, and pesticides from aqueous medium), as disinfectants (by removing microbes such as bacteria, fungi and viruses from aqueous medium), and as microbicides (to kill fungal, bacterial etc., pests, and as protective seed coat treatments), as anti microbial active ingredients in detergents, cleaning solutions and toxic gas detoxificants.

These functional transition metal silicates have many applications, which are useful in manufacturing of effective catalysts and anti-microbial paints etc.

BACKGROUND OF THE INVENTION

Extensive work is being carried out on zeolites and alkaline earth metal silicates compared to transition metal silicates.

In relation to transition metal silicates use for decontamination, Dodwell etal (U.S. Pat. No. 5,053,139, 1991) prepared transition metal silicates such as titanium and tin silicates, comprising cation exchangers, to remove heavy metals such as lead, cadmium, zinc, chromium and arsenic. When these metal silicates were failed to reduce the metal pollutant concentration, these metal silicates comprising with cation exchangers were prepared to reduce the metal pollutant concentration to required level. Although in patent claims, it was not mentioned about zirconium silicate (U.S. Pat. No. 5,053,139, 1991) but in the description (example 14) it was mentioned about zirconium silicate preparation along with cation exchanger, and the failure of zirconium silicate ion exchanger to reduce metal pollutant concentration in treated water.

It was observed that tin and titanium silicates failed to decontaminate coliform bacteria in drinking water when they were tested in our laboratory.

In the transition metals, anti-microbial metals such as silver, copper, zinc and manganese were well known and silicates of these metals were not studied in detail for the relation between function (such as decontamination, disinfection and microbicidal properties) and structural composition.

Copper silicates were known from 1936 (GB 442664) for agricultural or horticultural pest control and these copper silicates were synthesized by heating an aqueous suspension of finely divided hydrated silica with substantially insoluble basic copper compounds in alkaline conditions at high temperature.

The synthesis of various types of copper silicates based on the functional property was not studied among these reports or observations.

Many copper salts were formulated for use as agricultural pesticides and copper silicates do not gain much importance among them. Copper alumino silicates were mixed with antibiotics to obtain synergism between copper compounds and antibiotics (GB 788668).

Present invention is aimed to synthesize functional transition metal silicates of the required structural composition for targeted activities such as decontamination, disinfection and microbicidal properties etc. Another objective of the present invention is to invent novel immobilized functional transition metal silicates.

OBJECTS OF THE INVENTION

Accordingly it is the primary object of the invention is to invent functional transition metal silicates by synthesizing of the required structural composition for the targeted activities.

Another objective of invention is to invent functional transition metal silicates suitable for effective disinfection of microbes such as bacteria, fungi and viruses.

It is also the object of the invention is to invent transiton metal silicates suitable for effective decontamination of metals, chemical pollutants, and pesticides from aqueous systems.

Another objective of the invention is to invent functional transition metal silicates having microbicidal property for their usage as pesticides.

Another objective of invention is to develop functional transition metal silicates that are useful in mixing with seed coat treatments, paints, detergents, cleaning solutions, and zeolites.

Another object of the invention is to invent immobilized functional transition metal silicates, which are suitable to use in column mode as decontaminants (by sequestering metals, chemicals, and pesticides from aqueous medium), as disinfectants (by removing microbes such as bacteria, fungi and viruses from aqueous medium), and as microbicides (to kill fungal, bacterial etc., pests, and as protective seed coat treatments), as antimicrobial active ingredients in detergents, cleaning solutions and toxic gas detoxificants.

Another objective of the invention is to develop method for producing immobilized functional transition metal silicates by incorporating into resins, which are suitable for column mode decontaminants (by sequestering metals, chemicals, and pesticides from aqueous medium) as disinfectants (by removing microbes such as bacteria, fungi and viruses from aqueous medium), and as microbicides (to kill fungal, bacterial etc., pests, and as protective seed coat treatments), as antimicrobial active ingredients in detergents, cleaning solutions and toxic gas detoxificants.

Yet another object of the present invention is to develop immobilized functional transition metal silicates by coating transition metal silicate containing resins on quartz sand, which are suitable for column mode as decontaminants (by sequestering metals, chemicals, and pesticides from aqueous medium), as disinfectants (by removing microbes such as bacteria, fungi and viruses from aqueous medium), and as microbicides (to kill fungal, bacterial etc. pests, and as protective seed coat treatments), as antimicrobial active ingredients in detergents, cleaning solutions and toxic gas detoxificants.

SUMMARY OF THE INVENTION

To meet the above objects and others, the present invention provides novel functional transition metal silicates and immobilized functional transition metal silicates comprising required structural composition for targeted activities, and method of producing and utilizing these functional transition metal silicates for various purposes such as decontamination, disinfection, microbicidal, toxic gas detoxification from combustion, nicotine and tar detoxification from cigarette smoke etc. properties as defined in claims.

DETAILED DESCRIPTION OF THE INVENTION

Accordingly, the present invention provides a novel functional transition metal silicates (FTMS) selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate, said metal silicates being obtained by mixing salt solution of transition metal with a soluble alkaline silicate solution under desired pH, temperature and silicate to metal ratio and or by using immobilized form of functional transition metal silicates immobilized on materials selected from activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, and functional transition metal silicates incorporated resins and functional transition metal silicate containing resin coating on solid matrix such as quartz sand to obtain varied silicate metal ratio along with suitable structural composition for achieving effective functional transition metal silicate materials such as decontaminants of metals, chemicals, pesticides, disinfectants of bacteria, fungus and viruses, microbicides of pathogens such as bacteria and fungus, detoxificants of carbon monoxide, sulphur dioxide, NOX (oxides of nitrogen), hydrocarbons, tobacco tar, and nicotine etc.

More particularly, the present invention provides a novel functional transitional metal silicate selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate, said metal silicates being obtained by mixing salt solution of chloride, nitrates or sulphates of the corresponding transitional metals, with a soluble alkaline silicate solution under desired pH, temperature and silicate to metal ratio to form a precipitate, followed by washing and drying the precipitate to obtain the transition metal silicates varied silicate to metal ratio along with suitable structural composition, said transitional metal silicates exhibiting functions selected from decontamination, disinfection, microbicidal, detoxificant and anti-microbial.

IN an embodiment of the present invention, there is provided a functional transition metal silicate (FTMS) effective as a decontaminant, a disinfectant, a detoxificant, a protectant, a microbicide or combination thereof, comprising a ratio of transition metal to silica in the transition metal silicate in a predetermined range and a structural composition for said effectiveness, said FTMS being capable of being immobilized on a suitable materials or incorporating into resins and/or coating along with resins on suitable materials.

In another embodiment of the present invention, wherein a transition metal, wherin said ratio of transition metal to silica in the transition metal silicate is in a range of about 0.34 to about 19.57.

In yet another embodiment of the present invention, wherein a transition metal, comprising variable functions even with similar transition metal silicate ratio based on structural composition having specific ESR(g) values and specific XRD pattern obtained by varied reaction conditions.

In still another embodiment of the present invention, wherein the varied reaction conditions as claimed are varied pH conditions during a process for preparing the transitional metal silicates including extreme acidic to 12 PH, reactant concentrations: silicate content in soluble alkaline silicate solution and ratio of transition metal salt solution to soluble alkaline silicate solution, varied temperature maintained between 20 to 95 degrees centigrade, and combinations thereof.

In one more embodiment of the present invention, wherein the transition metal silicate is selected from the group consisting of cupric silicate, silver silicate, manganese silicate, zinc silicate, zirconium silicate and combination thereof.

In one another embodiment of the present invention, wherein the transition metal silicate is effective as a decontiminant of metals, chemicals, pesticides, microbes or combination thereof.

In a further embodiment of the present invention, wherein the transition metal silicate is effective as a disinfectant of a bacteria, a fungus, a virus, a microbicide of a pathogen or combinations thereof.

In a further more embodiment of the present invention, wherein the transition metal silicate is effective as a detoxificant of carbon monoxide, sulphur dioxide, an oxide of nitrogen, a hydrocarbon, tobacco tar, nicotine or toxic gases or chemical conversion of toxic gases and/or toxic chemical containing gases into non-toxic form, or combinations thereof.

In an embodiment of the present invention, wherein the metals are arsenic, mercury, lead, toxic metals or combinations thereof.

In another embodiment of the present invention, wherein the bacteria is a coliform bacteria, a Gram positive, a Gram negative bacteria or combinations thereof.

In yet another embodiment of the present invention, wherein the fungus is pathogenic fungi such as Sclerotium rolfsii, Rhizoctonia solani, Fusarium oxysporium, Pyricularia oryzae or combinations thereof.

In still another embodiment of the present invention, wherein the virus is having infective in nature.

In one more embodiment of the present invention, wherein the transition metal silicate is prepared by a method comprising:

-   -   (a) adding a solution of the transition metal to a soluble         alkali silicate solution to form a mixture;     -   (b) adjusting pH and/or temperature of the mixture;     -   (c) forming a precipitate comprising the transition metal         silicate;

(d) washing and drying the precipitate to obtain the transitional metal silicate.

In one another embodiment, the present invention provides a composition comprising a transition metal silicate immobilized on a substance, the transition metal silicate comprising a transition metal, wherein a ratio of transition metal to silica in the transition metal silicate is in a range of about 0.34 to about 19.57 and/or with a functional structure and the transition metal silicate is effective as a decontaminant, a disinfectant, a detoxificant or microbicide or combination thereof.

In a further embodiment of the present invention, wherein the substance is selected from a group consisting of an agropolymer, activated alumina, aluminium oxide, cellulose, vinyl ester resin, a bisphenol resin, an isopthalic food grade resin, quartz sand, silica gel and combinations thereof.

In a further more embodiment, the present invention provides a composition comprising a transition metal silicate incorporated in a substance, the transition metal silicate comprising a transition metal, wherein a ratio of transition metal to silica in the transition metal silicate is in a range of about 0.34 to about 19.57 and/or with functional structure and the transition metal silicate is effective as a decontaminant, a disinfectant, a detoxificant or microbicide or combination thereof.

In an embodiment of the present invention, wherein the substance is a resin.

In another embodiment of the present invention, wherein the resin is selected from a group consisting of a vinyl ester resin, a bisphenol resin, a isopthalic food grade resin and combinations thereof.

In yet another embodiment, the present invention provides a composition for a coating comprising a transition metal silicate comprising a transition metal, wherein a ratio of transition metal to silica in the transition metal silicate is in a range of about 0.34 to about 19.57 and/or with a functional structure and the transition metal silicate is effective as a decontaminant, a disinfectant, a detoxificant, a microbicide or combination thereof.

In still another embodiment of the present invention, wherein the coating further comprises a resin and a solid material.

In one more embodiment of the present invention, wherein the transition metal silicate is selected from the group consisting of cupric silicate, silver silicate, manganese silicate, zinc silicate, zirconium silicate and combination thereof.

In one another embodiment of the present invention, wherein the transition metal silicate is effective as a decontiminant of a metal, a chemical, a pesticide or microbe or combination thereof.

In a further embodiment of the present invention, wherein the transition metal silicate is effective as a disinfectant of a bacteria, a fungus, a virus, a microbe of a pathogen or combinations thereof.

In a further more embodiment of the present invention, wherein the transition metal silicate is effective as a detoxificant of toxic gases and/or toxic chemicals in gaseous forms such as carbon monoxide, sulphur dioxide, an oxide of nitrogen, a hydrocarbon, tobacco tar, nicotine or conversion of toxic gases to non-toxic gases or combinations thereof.

In an embodiment of the present invention, wherein when the functional transition metal silicate is a cupric silicate which is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution and 10 ml of sodium silicate solution having sodium and silica in the ratio 1:2 under acidic pH conditions have the following characteristic:

Silica: transition metal ratio as =1:5.15 (compositional analysis for silica /transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 4.32481 B) 2.55205 C) 2.31749 D) 2.08807 E) 2.04673

X-ray diffraction analysis give XRD significant peak height (counts/s) and angle ° 2 theta=1) 2128.25 and 16.28197

2) 1593.74 and 32.29018

3) 1470.73 and 39.79307

In another embodiment of the present invention, wherein when the functional transition metal silicate is a cupric silicate which is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution and 50 ml sodium silicate solution having sodium and silica in the ratio 1:1 at temperature in the range of 70° C. to 90° C. under acidic pH conditions have the following characteristic:

Silica: transition metal ratio as=1:0.78 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 2.23480 B) 2.06456

X-ray diffraction analysis give XRD significant peak height (counts/s) and angle ° 2 theta =1) 835.63 and 16.20057

2) 706.74 and 32.23910

3) 502.52 and 39.57159

In yet another embodiment of the present invention, wherein when the functional transition metal silicate is a cupric silicate which is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution and desired amount of sodium silicate solution having sodium and silica in the ratio 1:1 under neutral pH conditions have the following characteristic:

Silica: transition metal ratio as=1:1 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 3.10383 B) 2.36522 C) 2.0467 D) 1.21887 E) 0.96688

X-ray diffraction analysis give XRD significant peak height (counts/s) and angle ° 2 theta=1) 940.91 and 16.19577

2) 764.43 and 32.29276

3) 694.85 and 39.77809

In one more embodiment of the present invention, wherein when the functional transition metal silicate is a cupric silicate which is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution and desired amount of sodium silicate solution having sodium and silica in the ratio 1: 1 under basic pH conditions have the following characteristic:

Silica: transition metal ratio as=1:0.8 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 3.71806 B) 3.23001 C) 2.6168

X-ray diffraction analysis give XRD significant peak height (counts/s) and angle ° 2 theta=1)152.74 and 26.64983

In one another embodiment of the present invention, wherein when the functional transition metal silicate is a cupric silicate which is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution, 10 ml of 36% HCl and 50 ml of sodium silicate solution having sodium and silica in the ratio 1:1 at temperature in the range of 70° C. to 90° C. and under extreme acidic pH conditions have the following characteristic:

Silica: transition metal ratio as=1:0.53 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 2.18421 B) 2.06874 C) 1.21231

X-ray diffraction analysis give XRD significant peak height (counts/s) and Angle ° 2 theta=1) 400.70 and 16.19872

2) 394.77 and 32.27956

3) 330.02 and 39.71761

In a further embodiment of the present invention, wherein when the functional transition metal silicate is a cupric silicate which is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution, 20 ml of 36% HC1 and 50 ml of sodium silicate solution having sodium and silica in the ratio 1:1 at temperature in the range of 70° C. to 90° C. and under extreme acidic pH conditions have the following characteristic:

Silica: transition metal ratio as=1:0.34 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 2.15561 B) 2.03614

X-ray diffraction analysis give XRD significant peak height (counts/s) and Angle ° 2 theta=1) 541.23 and 16.26305

2) 414.21 and 32.36589

3) 365.45 and 39.85131

In an embodiment of the present invention, wherein when the functional transition metal silicate is a zinc silicate which is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution and desired quantity of sodium silicate solution having sodium and silica in the ratio 1:1 under neutral pH conditions have the following characteristic:

Silica: transition metal ratio as=1:12.13 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 5.49809 B) 4.55342 C) 2.54593 D) 2.10091 E) 2.05499

X-ray diffraction analysis give XRD significant peak height (counts/s) and Angle ° 2 theta=1) 444.15 and 32.75904

2) 307.02 and 59.58455

3) 263.36 and 28.27636

In another embodiment of the present invention, wherein when the functional transition metal silicate is a zinc silicate which is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution, 10 ml of 36% HCl and 50 ml of sodium silicate solution having sodium and silica in the ratio 1: 1 at temperature in the range of 70° C. to 90° C. and under extreme acidic pH conditions have the following characteristic:

Silica: transition metal ratio as=1:2.46 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 4.38410 B) 4.01910 C) 2.53191 D) 1.87886 E) 2.01793

X-ray diffraction analysis give XRD significant peak height (counts/s) and Angle ° 2 theta=1) 2079.88 and 11.07467

2) 835.44 and 33.52527

3) 664.98 and 32.88120

In yet another embodiment of the present invention, wherein when the functional transition metal silicate is a silver silicate which is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution and desired amount of sodium silicate solution having sodium and silica in the ratio 1:2 under neutral pH conditions have the following characteristic:

Silica: transition metal ratio as=1:19.57 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 4.36796 B) 2.37847 C) 3.95509 D) 2.04657

X-ray diffraction analysis give XRD significant peak height (counts/s) and Angle ° 2 theta=1) 3945.11 and 32.29885

2) 2421.27 and 46.27446

3) 1835.66 and 27.89129

In still another embodiment of the present invention, wherein when the functional transition metal silicate is a silver silicate which is synthesized by mixing 50 ml of 0.5 gm/ml transition metal salt solution, 8 ml of 69-70% HNO₃ and desired amount of sodium silicate solution having sodium and silica in the ratio 1:1 under acidic pH conditions (about 2 pH) have the following characteristic:

Silica: transition metal ratio as=1:1.04 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 4.37171 B) 4.04714 C) 1.98189

X-ray diffraction analysis give XRD significant peak height (counts/s) and Angle ° 2 theta=1) 2217.87 and 29.33483

2) 684.55 and 47.68093

3) 674.27 and 42.31091

In one more embodiment of the present invention, wherein when the functional transition metal silicate is a manganese silicate which is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution and desired amount of sodium silicate solution having sodium and silica in the ratio 1:1 under neutral pH conditions have the following characteristic:

Silica: transition metal ratio as=1:1.94 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 1.93412 B) 2.06655

X-ray diffraction analysis give XRD significant peal( height (counts/s) and Angle ° 2 theta=1) 148.04 and 30.65087

In one another embodiment of the present invention, wherein when the functional transition metal silicate is a manganese silicate which is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution, 10 ml of 36% HCl and 50 ml of sodium silicate solution having sodium and silica in the ratio 1:1 at temperature in the range of 70° C. to 90° C. and under extreme acidic pH conditions have the following characteristic:

Silica: transition metal ratio as=1:1.09 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 4.3463 B) 4.17458 C) 2.18228 D) 2.11243 E) 2.05491 F) 1.999661

X-ray diffraction analysis give XRD significant peak height (counts/s) and Angle ° 2 theta=1) 32.88 and 24.65599

In a further embodiment of the present invention, wherein when the functional transition metal silicate is a zirconium silicate which is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution and desired amount of sodium silicate solution having sodium and silica in the ratio 1:1 under neutral pH conditions have the following characteristic:

Silica: transition metal ratio as=1:2.90 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 4.42797 B) 4.18272 C) 2.24547 D) 2.30425 E) 2.18961 F) 1.23086

In an embodiment of the present invention, wherein when the functional transition metal silicate is a zirconium silicate which is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution, 10 ml of 36% HCl and 50 ml of sodium silicate solution having sodium and silica in the ratio 1:1 at temperature in the range of 70° C. to 90° C. and under extreme acidic pH conditions have the following characteristic:

Silica: transition metal ratio as=1:0.77 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 4.37236 B) 2.82039 C) 1.92596 D) 1.21652 E) 1.02930 F) 0.93795

X-ray diffraction analysis give XRD significant peak height (counts/s) and Angle ° 2 theta=1) 84.80 and 10.89433

The present invention also provides a functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate, said metal silicates being obtained by mixing salt solution of chloride, nitrates or sulphates of the corresponding transitional metals, with a soluble alkaline silicate solution under desired pH, temperature and silicate to metal ratio to form a precipitate, followed by washing and drying the precipitate and having the structure as shown in FIGS. 1 to 14 of the accompanying drawings and said transitional metal silicates exhibiting functions selected from decontamination, disinfection, microbicidal and anti-microbial.

In an embodiment of the present invention, wherein the functional metal silicates are optionally loaded or coated on a substrate selected from activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, and functional transition metal silicates incorporated resins and functional transition metal silicate containing resin coated on solid matrix selected from quartz sand.

The present invention also provides a method of decontaminating an aqueous medium containing sequestering metals, chemicals and pesticides, said method containing the step of contacting the aqueous medium with a novel functional transition metal silicates (FTMS) selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate optionally loaded or coated on a substrate in a container.

In an embodiment of the present invention, wherein the transitional metal silicates synthesized under acidic pH conditions and extremely acidic pH conditions provide better decontamination as compared to transitional metal silicates synthesized under basic and neutral pH conditions.

The present invention further provides a method of disinfecting an aqueous medium containing microbes, bacteria, fungi and viruses, said method containing the step of contacting the aqueous medium with a novel functional transition metal silicates (FTMS) selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate optionally loaded or coated on a substrate in a container.

In an embodiment of the present invention, wherein the transitional metal silicates synthesized under acidic pH conditions and extremely acidic pH conditions provide decontamination and disinfection of microbes.

In another embodiment of the present invention, wherein the transitional metal silicates synthesized provide protection and/or control of pathogenic viruses.

In yet another embodiment of the present invention, wherein the transitional metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate optionally loaded or coated on a substrate in a container disinfect gram positive and gram negative bacteria, fungus, and viruses enabling the usage of these novel functional transition metal silicates in detergents, cleaning solutions, seed coat treatments, disinfectants, and shampoos etc., for protection against microbial infections.

The present invention further more provides a process for preparing novel functional transition metal silicates (FTMS), selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate, said process comprising the steps of:

-   -   (a) addition transition metal salt solution to a soluble alkali         silicate solution;     -   (b) selecting pH conditions of reaction i.e., acidic, or         neutral, or basic or extreme acidic conditions (by adding acid         such as HCl or HNO₃ to reaction medium) to form a precipitate,         and     -   (c) drying the resultant precipitate of functional transition         metal silicate without any soluble substances after through         washing with distilled or deionized water to obtain the         functional transition metal silicates.

In an embodiment of the present invention, wherein the functional transition metal silicates having varied silicate metal ratio were synthesized and silicate or transition metal content enhancement or decrease in a functional transition metal silicates was done at suitable reaction conditions selected from acidic or neutral or basic or extreme acidic pH conditions and using varied concentration of reactants selected from soluble silica having different alkali to silica ratio.

In another embodiment of the present invention, wherein cupric silicate having the characteristic as given below is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution and 10 ml of sodium silicate solution having sodium and silica in the ratio 1:2 under acidic pH conditions.

Silica: transition metal ratio as=1:5.15 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 4.32481 B) 2.55205 C) 2.31749 D) 2.08807 E) 2.04673

X-ray diffraction analysis give XRD significant peak height (counts/s) and angle ° 2 theta=1) 2128.25 and 16.28197

2) 1593.74 and 32.29018

3) 1470.73 and 39.79307

In yet another embodiment of the present invention, wherein a cupric silicate having the characteristics as given below is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution and 50 ml sodium silicate solution having sodium and silica in the ratio 1:1 at temperature in the range of 70° C. to 90° C. under acidic pH conditions.

Silica: transition metal ratio as=1:0.78 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 2.23480 B) 2.06456

X-ray diffraction analysis give XRD significant peak height (counts/s) and angle ° 2 theta=1) 835.63 and 16.20057

2) 706.74 and 32.23910

3) 502.52 and 39.57159

In still another embodiment of the present invention, wherein a cupric silicate having the characteristics as given below synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution and desired amount of sodium silicate solution having sodium and silica in the ratio 1:1 under neutral pH conditions.

Silica: transition metal ratio as=1:1 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 3.10383 B) 2.36522 C) 2.0467 D) 1.21887 E) 0.96688

X-ray diffraction analysis give XRD significant peak height (counts/s) and angle ° 2 theta=1) 940.91 and 16.19577

2) 764.43 and 32.29276

3) 694.85 and 39.77809

In one more embodiment of the present invention, wherein cupric silicate having the characteristics as given below is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution and desired amount of sodium silicate solution having sodium and silica in the ratio 1:1 under basic pH conditions have the following characteristic:

Silica: transition metal ratio as=1:0.8 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 3.71806 B) 3.23001 C) 2.6168

X-ray diffraction analysis give XRD significant peak height (counts/s) and angle ° 2 theta=1) 152.74 and 26.64983

In one another embodiment of the present invention, wherein cupric silicate having the characteristics as given below is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution, 10 ml of 36% HCl and 50 ml of sodium silicate solution having sodium and silica in the ratio 1:1 at temperature in the range of 70° C. to 90° C. and under extreme acidic pH condition.

Silica: transition metal ratio as=1:0.53 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 2.18421 B) 2.06874 C) 1.21231

X-ray diffraction analysis give XRD significant peak height (counts/s) and Angle ° 2 theta=1) ⁴00.70 and 16.19872

2) 394.77 and 32.27956

3) 330.02 and 39.71761

In a further embodiment of the present invention, wherein cupric silicate having the characteristics as given below is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution, 20 ml of 36% HCl and 50 ml of sodium silicate solution having sodium and silica in the ratio 1:1 at temperature in the range of 70° C. to 90° C. and under extreme acidic pH conditions.

Silica: transition metal ratio as=1:0.34 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 2.15561 B) 2.03614

X-ray diffraction analysis give XRD significant peak height (counts/s) and Angle ° 2 theta=1) 541.23 and 16.26305

2) 414.21 and 32.36589

3) 365.45 and 39.85131

In a further more embodiment of the present invention, wherein zinc silicate having the characteristics as given below is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution and desired quantity of sodium silicate solution having sodium and silica in the ratio 1:1 under neutral pH conditions.

Silica: transition metal ratio as=1:12.13 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 5.49809 B) 4.55342 C) 2.54593 D) 2.10091 E) 2.05499

X-ray diffraction analysis give XRD significant peak height (counts/s) and Angle ° 2 theta=1) 444.15 and 32.75904

2) 307.02 and 59.58455

3) 263.36 and 28.27636

In an embodiment of the present invention, wherein zinc silicate having the characteristics as given below is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution, 10 ml of 36% HCl and 50 ml of sodium silicate solution having sodium and silica in the ratio 1:1 at temperature in the range of 70° C. to 90° C. and under extreme acidic pH conditions have the following characteristic:

Silica: transition metal ratio as=1:2.46 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 4.38410 B) 4.01910 C) 2.53191 D) 1.87886 E) 2:.01793

X-ray diffraction analysis give XRD significant peak height (counts/s) and Angle ° 2 theta=1) 2079.88 and 11.07467

2) 835.44 and 33.52527

3) 664.98 and 32.88120

In another embodiment of the present invention, wherein silver silicate having the characteristics as given below is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution and desired amount of sodium silicate solution having sodium and silica in the ratio 1:2 under neutral pH conditions.

Silica: transition metal ratio as=1:19.57 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 4.36796 B) 2.37847 C) 3.95509 D) 2.04657

X-ray diffraction analysis give XRD significant peak height (counts/s) and Angle ° 2 theta=1) 3945.11 and 32.29885

2) 2421.27 and 46.27446

3) 1835.66 and 27.89129

In yet another embodiment of the present invention, wherein silver silicate having the characteristics as given below is synthesized by mixing 50 ml of 0.5 gm/ml transition metal salt solution, 8 ml of 69-70% HNO₃ and desired amount of sodium silicate solution having sodium and silica in the ratio 1:1 under acidic pH conditions (about 2 pH).

Silica: transition metal ratio as=1:1.04 (compositional analysis for silica/transition metal ratio).

Electron Spin Resonance ESR (g values)=A) 4.37171 B) 4.04714 C) 1.98189

X-ray diffraction analysis give XRD significant peak height (counts/s) and Angle ° 2 theta=1) 2217.87 and 29.33483

2) 684.55 and 47.68093

3) 674.27 and 42.31091

In still another embodiment of the present invention, wherein magnesium silicate having the characteristics as given below is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution and desired amount of sodium silicate solution having sodium and silica in the ratio 1:1 under neutral pH conditions have the following characteristic:

Silica: transition metal ratio as=1:1.94 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 1.93412 B) 2.06655

X-ray diffraction analysis give XRD significant peak height (counts/s) and Angle ° 2 theta=1) 148.04 and 30.65087

In one more embodiment of the present invention, wherein manganese silicate having the characteristics as given below is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution, 10 ml of 36% HCl and 50 ml of sodium silicate solution having sodium and silica in the ratio 1:1 at temperature in the range of 70° C. to 90° C. and under extreme acidic pH conditions have the following characteristic:

Silica: transition metal ratio as=1:1.09 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 4.3463 B) 4.17458 C) 2.18228 D) 2.11243 E) 2.05491 F) 1.999661

X-ray diffraction analysis give XRD significant peak height (counts/s) and Angle ° 2 theta=1) 32.88 and 24.65599

In one another embodiment of the present invention, wherein zirconium silicate having the characteristics as given below is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution and desired amount of sodium silicate solution having sodium and silica in the ratio 1:1 under neutral pH conditions have the following characteristic:

Silica: transition metal ratio as=1:2.90 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 4.42797 B) 4.18272 C) 2:24547 D) 2.30425 E) 2.18961 F) 1.23086

In a further embodiment of the present invention, wherein zirconium silicate having the characteristics as given below is synthesized by mixing 100 ml of 0.5 gm/ml transition metal salt solution, 10 ml of 36% HCl and 50 ml of sodium silicate solution having sodium and silica in the ratio 1:1 at temperature in the range of 70° C. to 90° C. and under extreme acidic pH conditions have the following characteristic:

Silica: transition metal ratio as=1:0.77 (compositional analysis for silica/transition metal ratio)

Electron Spin Resonance ESR (g values)=A) 4.37236 B) 2.82039 C) 1.92596 D) 1.21652 E) 1.02930 F) 0.93795

X-ray diffraction analysis give XRD significant peak height (counts/s) and Angle ° 2 theta=1) 84.80 and 10.89433

In a further more embodiment of the present invention, wherein functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate are capable of decontaminate heavy metals such as arsenic, mercury, etc., thereby enabling them to use these novel functional transitional metal silicates to decontaminate aqueous media such as metal polluted drinking water, ground water, industrial pollutants and any other sources of metal pollution.

In an embodiment of the present invention, wherein functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate decontaminate pollutant chemicals such as trihalomethanes, polychlorinated biphenyls, semi volatile organic compounds, volatile organic compounds, and phenols.

In another embodiment of the present invention, wherein functional transition metal silicates control plant pathogens such as Sclerotium rolfsii, Rhizoctonia solani, Fusarium oxysporium, Pyricularia oryzae and this property enables functional transition metal silicates usage as effective pesticides.

The present also provides a process for preparing immobilized functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate immobilized on a substrate material selected from agropolymers, activated alumina, cellulose, aluminium oxide, quartz sand, silica gel and suitable for use in column or batch mode, said process comprising the steps of:

-   -   (a) adding transition metal salt containing solution selected         from chlorides or sulphates or nitrates to the substrate         material selected from agropolymers, activated alumina,         cellulose, aluminium oxide, quartz sand, silica gel;     -   (b) mixing the transition metal salt solution loaded substrate         material of step (a) with alkali silicate solution;     -   (c) heating the mixture at 70° C. to 90° C. and allowing the         same to settle for 10 to 14 hrs at room temperature, and     -   (d) removing unbound or non-immobilized substances by extensive         washing with distilled or deionized water to obtain the         immobilized functional transition metal silicates.

In an embodiment of the present invention, wherein the amount of functional transition metal silicate immobilized on the substrate material varies based on initial concentration of transition metal salt, soluble silica, the reaction time, particle size of substrate material and type of substrate material, and mode of immobilization such as physical or chemical.

In another embodiment of the present invention, wherein the functional transition metal silicates are immobilized by physical or chemical means.

In yet another embodiment of the present invention, wherein the functional transitional metal silicates are immobilized upon a solid matrix like quartz sand which is suitable for column mode and batch mode decontamination by directly incorporating the functional transitional metal silicates into resins and coating the functional transition metal silicate containing resins on the quartz sand.

In still another embodiment of the present invention, wherein functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate immobilized on materials selected from activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, are capable of decontaminating metals such as arsenic, mercury, etc., and this property enables immobilized functional transition metal silicates utility to purify metal contaminated drinking water, ground water and any other metal polluted aqueous streams.

In one more embodiment of the present invention, wherein functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate immobilized on materials selected from activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, are capable of capable of disinfecting coliform bacteria, from water and this property enables immobilized functional transition metal silicate utility to purify water free of harmful microbes.

In one another embodiment of the present invention, wherein functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate immobilized on agropolymers are capable of decontaminating protozoan, Cryptosporidium parvum, from water and this property enables the usage of immobilized functional transition metal silicates for protection and or control of protozoan infections.

In a further embodiment of the present invention, wherein functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate immobilized on materials selected from activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, are capable of decontaminating polio viruses, rota viruses from water and this property enables their usage of immobilized functional transition metal silicates for protection and or control of pathogenic viruses infections.

The present invention further provides a process for preparing functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate containing resins, for use as decontaminants by sequestering metals, chemicals, and pesticides from aqueous medium, disinfectants by removing microbes such as bacteria, fungi and viruses from aqueous medium, microbicides by killing fungus, bacteria etc., protective seed coat, insect/pest repellent, anti microbe active ingredients in detergents, cleaning solutions and detoxificants of toxic gas, nicotine and tar in column and batch mode, said process comprising the steps of:

-   -   (a) adding 5 to 20% by wt. of the functional transition metal         silicates to the resins selected from vinyl ester, bisphenol,         isopthalic resins;     -   (b) drying the mixture of step (a) by heating at 70° C. to         90° C. without addition of catalysts or accelerators, and     -   (c) grinding the resultant material to required size.

In an embodiment of the present invention, wherein functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate incorporated into resins selected from vinyl ester, bisphenol, isopthalic resins, are capable of decontaminating metals such as arsenic, mercury, etc., and this property enables immobilized functional transition metal silicates utility to purify metal contaminated drinking water, ground water and any other metal polluted aqueous streams functional transition metal silicate containing resin coated sand

In another embodiment of the present invention, wherein functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate incorporated into resins selected from vinyl ester, bisphenol, isopthalic resins, are capable of disinfecting coliform bacteria, from water and this property enables immobilized functional transition metal silicate utility to purify water free of harmful microbes.

The present invention provides a process for preparing solid substances such as quartz sand, suitable for use as decontaminants by sequestering metals, chemicals, and pesticides from aqueous medium, as disinfectants by removing microbes such as bacteria, fungi and viruses from aqueous medium, as microbicides by killing fungus, bacteria, pests etc., as seed protectant, as anti microbial active ingredients in detergents, cleaning solutions and detoxificants of toxic gas, nicotine and tar etc:, coated with resins selected from vinyl ester, bisphenol, isopthalic resins containing functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate said process comprising the steps of:

-   -   (i) adding the functional transition metal silicates to the         resins in the w/v ratio ranging from 0.5:1 to 4:1;     -   (ii) mixing thoroughly the functional transition metal silicate         containing resin of step (i) with solid matrix selected from         quartz sand having size from 50-1000 microns at v/v ratio         ranging from 1:5 to 1:50, and     -   (iii) drying the resin-coated sand of step (ii) without addition         of any catalyst or accelerators at 70° C. to 90° C. or by         keeping at room temperature for a week to obtain the functional         transition metal silicate coated solid substance.

In an embodiment of the present invention, wherein functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate coated on sand is capable of decontaminating metals such as arsenic, mercury, etc., and this property enables immobilized functional transition metal silicates utility to purify metal contaminated drinking water, ground water and any other metal polluted aqueous streams.

In another embodiment of the present invention, wherein functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate coated on sand is capable of disinfecting coliform bacteria, from water and this property enables immobilized functional transition metal silicate utility to purify water free of harmful microbes.

In yet another embodiment of the present invention, wherein the functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate immobilized on materials selected from activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, or functional transition metal silicates incorporated into resins or sand coated with functional transition metal silicates containing resin are capable of detoxifying toxic gases such as carbon monoxide, sulphur dioxide, nitrous oxide and hydrocarbons from combustion gases and this property enables these immobilized functional transition metal silicate containing filters usage as toxic air purifiers.

In still another embodiment of the present invention, wherein the functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate immobilized on materials selected from activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, or functional transition metal silicates incorporated into resins or sand coated with functional transition metal silicates containing resin are capable of detoxifying cigarette smoke by significantly reducing carbon monoxide, sulphur dioxide, nitrous oxide hydrocarbons, tar and nicotine and this property enables these immobilized functional transition metal silicate containing filters usage as toxic air and chemical purifiers and/or chemical conversion of toxic gases to non-toxic gases.

In one more embodiment of the present invention, wherein the functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate immobilized on materials selected from activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, or functional transition metal silicates incorporated into resins or sand coated with functional transition metal silicates containing resin are capable of decontaminating pesticides selected from chlorinated hydrocarbons such as endosulphan, synthetic pyrethroides such as cypermethrin, organophosphates such as chloripyriphos and this property enables these immobilized functional transition metal silicates as decontaminants of pesticides.

In one another embodiment of the present invention, wherein the functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate immobilized on materials selected from activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, or functional transition metal silicates incorporated into resins or sand coated with functional transition metal silicates containing resin are capable of decontaminating proteins from an aqueous medium enabling their usage to remove or decontaminate proteins from waste waters generating from bioprocess industry, to prevent undesirable protein contamination.

In a further embodiment of the present invention, wherein the functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate immobilized on materials selected from activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, or functional transition metal silicates incorporated into resins or sand coated with functional transition metal silicates containing resin are capable of decontaminating fungus from water and this property enables the usage of immobilized functional transition metal silicates for protection and or control of fungal infections.

In further more embodiment of the present invention, wherein the functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate immobilized on materials selected from activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, or functional transition metal silicates incorporated into resins or sand coated with functional transition metal silicates containing resin are capable of decontaminating trihalomethanes selected from chloroform, 1,1,1; trichloroethane, tetrachloroethylene, trichloroethylene, bromodichloroethane, dibromochloroethane, tetrachloroethylene, bromoform and 1,2, dichloro-3-bromopropane.

In an embodiment of the present invention, wherein the functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate immobilized on materials selected from activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, or functional transition metal silicates incorporated into resins or sand coated with functional transition metal silicates containing resin are capable of decontaminating Polychlorinated biphenyls selected from 2,3-dichlorobiphenyl, trichlorobiphenyl, tetrachlorobiphenyl, pentachlorobiphenyl, hexachlorobiphenyl, heptachlorobiphenyl and octachlorobiphenyl.

In another embodiment of the present invention, wherein the functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate immobilized on materials selected from activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, or functional transition metal silicates incorporated into resins or sand coated with functional transition metal silicates containing resin are capable of decontaminating volatile organic compounds selected from 1,1,1, trichloroethane; 1,1,2-trichloroethane; 1,3-dichloropropane; dibromochloromethane; ethane 1,2 dibromo; chlorobenzene; benzene 1,2-dimethyl; benzene 1,3-dimethyl; orthoxylene; benzene 1-methylethyl; ethane 1,1,2,2-tetrachloro; bromobenzene; 2-chloro toluene; benzene, propyl; benzene, 1chloro 4-methyl; benzene 1,2,3-trimethyl; 4-iso propyl toluene; benzene 1,2-diethyl; benzene 1,2-dichloro; 1,3-dichlorobenzene; 1,4-dichlorobenzene; toluene; n-butylbenzene; 1,2-dibromo 3-chloropropane; 1,2,4-trichlorobenzene; naphthalene; benzene 1,2,3-trichloro; benzene 1,3,5-trichloro; benzene 1,3,4-trichloro; 1,3-butadienel,1,2,3,4; benzene 2-bromo 1,3,5; nitrobenzene; styrene; benzylbenzoate; 1,2,3,4-tetramethylbenzene; benzene 1-chloro 2-propyl and 4-bromo 3-chloroanilene.

In yet another embodiment of the present invention, wherein the functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate immobilized on materials selected from activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, or functional transition metal silicates incorporated into resins or sand coated with functional transition metal silicates containing resin are capable of decontaminating semi volatile organic compounds (such as benzene, 1,4-dichloro; ethane hexachloro; benzene 1,2,3, trichloro; 1,3 butadiene, 1,1,2,3,4; naphthalene, 2-chloro; acenephthylene; acenapthene; phenol, 2,4-bis(1,1-imet); diethyl phthalate; fluorene; benzenel-chloro-3phenol; diphenylamine; 4-bromophenyl-phenylether; benzene, hexachloro; phenantherene; anthracene; dibutyl phthalate; fluoranthene; pyrene; benzyl butyl phthalate; chrysene; bis(2-ethylhexy)phthalate; phenol, 2,3,4,5-tetrabrom; di-n-octyl phthalate; benzo (b) fluoranthene; benzo(k) fluoranthene; benzo(a) pyrene; indeno(1,2,3-cd) pyrene; dibenzo(a,h) anthracene and benzo(g,h,l) perylene.

In still another embodiment of the present invention, wherein the functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate immobilized on materials selected from activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, or functional transition metal silicates incorporated into resins or sand coated with functional transition metal silicates containing resin are capable of decontaminating phenols (such as benzoic acid; 2,4,5-trichlorophenol; 3-nitroaniline; 3-nitrophenol; 4-nitrophenol; 2,4-dinitrophenol; 4-nitroaniline and pentachlorophenol.

In one more embodiment of the present invention, wherein the functional transition metal. silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate immobilized on materials selected from activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, or functional transition metal silicates incorporated into resins or sand coated with functional transition metal silicates containing resin have utility of decontamination and disinfection in high temperature zones such as boilers etc., due to thermo stability of this material.

In one another embodiment of the present invention, wherein the functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate immobilized on materials selected from activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, or functional transition metal silicates incorporated into resins or sand coated with functional transition metal silicates containing resin exhibited microbicidal nature against bacteria fungus and viruses enabling functional transition metal silicates usage as microbicides.

In a further embodiment of the present invention, wherein the functional transition metal silicates selected from cupric silicate, silver silicate, manganese silicate, zinc silicate and zirconium silicate optionally immobilized on materials selected from activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, or functional transition metal silicates incorporated into resins or sand coated with functional transition metal silicates containing resin and having varied metal silicate ratio exhibiting varied functions gives a method to obtain selective conjugates of transition metals along with silicates for obtaining functionally effective functional transition metal silicates to use in various other applications such as manufacturing of catalysts, and hybridizing or doping with zeolites.

In further more embodiment of the present invention, wherein achieving of an inclusion of a desired functionality in a selected functional transition metal silicate is attainable by optimization of synthetic conditions selected from inclusion of arsenic sequestation ability into silver silicate, inclusion of bacterial decontamination property into zirconium silicate, inclusion of effective microbicidal (bactericidal and fungicidal) property into cupric silicate.

Now this invention will be described in detail so as to illustrate and explain various salient features of the invention.

One embodiment of the invention is to provide functional transition metal silicates to decontaminate metals, chemicals and disinfect microbes.

Synthesis of Functional Transition Metal Silicates:

The synthesis of various types of functional transition metal silicates were attained by reacting with different concentrations of transition metal salt solution with soluble silica containing alkali (with different silica alkali ratio) and at variable reaction conditions such as pH, and temperature.

Now this invention will describe one of the methods used in synthesis of functional transition metal silicates.

Transition metal salt solution (chlorides or nitrates or sulphates) was reacted to soluble silica. The soluble silica in alkaline medium was prepared by various ways, such as dissolving of sodium silicate or potassium silicate in water (distilled or deionized) or by dissolving amorphous silica in alkali such as sodium hydroxide or potassium hydroxide in water (distilled or deionized). Varied silica to alkali ratios was obtained in a soluble silica solution, by dissolving the amorphous silica with required amount of alkali. Different concentrations of transition metal salt solution were reacted with soluble silica (containing varied amount of alkali) at different pH conditions along with varied temperatures of reaction to obtain various types of functional transition metal silicates. The precipitate obtained after reaction of transition metal salts with soluble silica was washed extensively with distilled or deionized water to remove soluble substances.

The resultant purified materials of functional transition metal silicates were analyzed by SEM/EDAX (ESEM, XL-30), ESR (JEOL, JES-FA-200), AND XRD (PHILIPS, PW-1830) and other analytical estimation procedures (such as AAS, ICP-AES etc.,) to understand the composition, structure etc., details.

These substances (functional transition metal silicates) were evaluated for their comparative functional properties such as decontamination, disinfection, microbicidal, toxic gas detoxification and nicotine and tar detoxification etc. properties.

The metal decontamination ability was assayed by estimating arsenic sequestration capacity of these different functional transition metal silicates. Arsenic containing water was treated with functional transition metal silicate and the sequestered arsenic content by functional transition metal silicate was estimated by AAS or ICP-AES.

The microbial disinfection ability of these functional transition metal silicates was assayed by measuring the amount of bacteria (coliform or enterobacteria) removed from contaminated drinking water. Coliform or enterobacteria containing polluted water was added to normal drinking water and bacterial amount present before and after treatment with functional transition metal silicates was assayed. The bacterial assay was done by counting the individual bacterial colonies, which were obtained by inoculating the bacteria containing water on petriplates containing growth media.

The comparative fungicidal nature of functional transition metal silicates was assayed against Sclerotium rolfsii, Rhizoctonia solani, Fusarium oxysporium, and Pyricularia oryzae, by poison food technique (by adding test materials in the growth medium of fungus and measuring the growth of the fungus in comparison with control). The radial growth of the fungus in the petriplates was measured and percent inhibition of the growth of the fungus was calculated.

The microbicidal activity of functional transition metal silicate was assayed against gram positive and gram negative bacteria such as Staphylococcus aureus, Bacillus subtilis, Pseudomonas aeruginosa, and Eschericia coli by mixing functional transition metal silicates in growth media of bacteria. The growth of bacteria in media containing functional transition metal silicate was compared with control (bacterial growth media without functional transition metal silicate) in petriplates.

The comparative bactericidal nature of functional transition metal silicate containing different metal and silicate ratio was assayed against bacteria by adding various concentrations (such as 0.06, 0.125, 0.25%) of functional transition metal silicates in growth media.

The viral decontamination ability of these functional transition metal silicates was assayed using bacteriophages in water by batch method.

The chemical pollutants decontamination ability of these functional transition metal silicates was assayed by addition of functional transition metal silicates to contaminant such as trihalomethanes (chloroform, 1,1,1, trichloroethane, tetrachloroethylene, trichloroethylene, bromodichloroethane, dibromochloroethane, tetrachloroethylene, bromoform, 1,2, dichloro-3-bromopropane) containing water. After thorough shaking of the functional transition metal silicates with chemical pollutants dissolved water for 15 minutes, the resultant water containing functional transition metal silicate was allowed to precipitate for two hours. The chemical pollutants content present in treated solution was assayed by using GC-FID or GC-ECD or GC/MS/MS.

One embodiment of the invention is to provide immobilized functional transition metal silicates to decontaminate (metals, chemicals, and pesticides), disinfect microbes (fungus, protozoa, bacteria, and viruses), and to detoxify toxic gases, nicotine and tar etc.

Transition metal (silver, copper, zinc, manganese, and zirconium) salt solution, (such as chlorides or nitrates or sulphates of these metals) was mixed with materials such as activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, and silica gel and corresponding immobilized transition metal silicate was obtained by treating with sodium silicate or potassium silicate solution. This process was achieved in another way by adding initially sodium silicate or potassium silicate solution to the materials such as activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, and silica gel and corresponding immobilized functional transition metal silicates were obtained by treating with salts of silver, cupric, zinc, manganese, and zirconium, (such as chlorides or nitrates or sulphates of these metals).

Transition metal (silver, copper, zinc, manganese, and zirconium) salt solution, (such as chlorides or nitrates or sulphates of these metals) was added to solution containing sodium silicate or potassium silicate to obtain respective functional transition metal silicate and thus obtained transition metal silicate was mixed with resins such as vinyl ester, or bisphenol resins, or isopthalic resins of food grade, without catalysts (such as cobalt octate) and allowed to polymerize after heating at 70° C. to 90° C. Later these materials were powdered to obtain desired particle size.

In a preferred embodiment the present invention provides a method of producing immobilized transition metal substances (silver silicate, cupric silicate, zinc silicate, manganese silicate, and zirconium silicate), said method comprising the following steps.

-   -   a) Addition of soluble transition metal salt solution to the         selected matrix for immobilization such as activated alumina,         aluminum oxide, bisphenol resins, agropolymers, cellulose,         quartz sand and silica gel.     -   b) Treating the matrix containing metal salts with solution of         sodium silicate or potassium silicate to obtain corresponding         metal silicate immobilized on matrix.     -   c) Washing extensively with distilled or deionized water to         remove unbound, non-immobilized substances from the matrix such         as activated alumina, aluminum oxide, agropolymers, cellulose,         quartz sand and silica gel.     -   d) Drying the resultant material either by centrifugation,         filtration and or by heating.

Another embodiment of the present invention relates to a method of production of immobilized functional transition metal silicates (silver silicate, cupric silicate, zinc silicate, manganese silicate, and zirconium silicate) by incorporating functional transition metal silicate into resins such as vinyl ester, or bisphenol resins, or isopthalic resins of food grade.

Another embodiment of the present invention relates to a method of production of immobilized functional transition metal silicates (silver silicate, cupric silicate, zinc silicate, manganese silicate, and zirconium silicate) containing resins (such as vinyl ester, or bisphenol resins, or isopthalic resins of food grade) coating on solid matrix like quartz sand.

Now this invention will describe one of the methods used in production of immobilized functional transition metal silicates. Most of these immobilizations were carried either at neutral reaction conditions (6-7 pH) or at acidic reaction conditions (2 pH).

These illustrations explained below do not limit the scope of invention i.e., production of immobilized functional transition metal silicates using various other matrixes along with varied reaction conditions.

Immobilization of Functional Transition Metal Silicates on Activated Alumina:

Transition metal salt solution (0.5 gm/ml) was added to activated alumina granules followed by alkali silicate solution (such as sodium silicate or potassium silicate-0.5 g/ml, alkali:silica=1:1) addition to obtain functional transition metal silicate immobilized on activated alumina. Various sizes of activated alumina (100-2000 micron size) were chosen to obtain immobilized functional transition metal silicates. Varied reaction times along with initial chemical concentrations were chosen for immobilization along with varied concentration of metal salts to alkali content as described earlier. The unbound, non-immobilized materials were removed by washing extensively with distilled or deionized water. The immobilization of functional transition metal silicate content was achieved to 1-9% (w/w) on activated alumina based on number of coatings, and different reaction conditions.

Immobilization of Functional Transition Metal Silicates on Aluminium Oxide:

The neutral aluminium oxide (column chromatography grade) was mixed with transition metal salt solution (0.5 g/ml) and later functional transition metal silicates formation and immobilization was done by addition of sodium silicate or potassium silicate solution (0.5 g/ml, alkali:silica=1:1). The unbound, non-immobilized materials were washed extensively with distilled or deionized water.

The immobilization of functional transition metal silicate content was achieved up to 2-10% (w/w) on aluminium oxide based on number of coatings.

Immobilization of Functional Transition Metal Silicates on Agropolymers:

Transition metal salts containing solution (0.5 g/ml) was added to various agropolymers derived from seed coats of various crops and functional transition metal silicates were immobilized by adding sodium silicate or potassium silicate solution at pH 3-4 (0.5 g/ml, alkali:silica=1:1). The unbound materials were washed extensively with distilled or deionized water to remove non-immobilized materials, and the resultant agropolymer containing functional transition metal silicate was dried at room temperature or by heating. The immobilized functional transition metal silicate content on agropolymers varied from 2-25 percent (w/w) based on number coatings.

Immobilization of Functional Transition Metal Silicates on Cellulose:

Micro crystalline, cellulose (column chromatography grade), was mixed with transition metal salt containing solution (0.5 g/ml) and immobilization was attained by adding sodium silicate or potassium silicate solution (0.5 g/ml, alkali:silica=1:1). The functional transition metal silicate immobilized materials were dried, after thorough washing with distilled or deionized water to remove unbound or non-immobilized materials. The immobilized functional transition metal silicate content on cellulose was achieved up to 3-10% (w/w) based on number of coatings.

Immobilization of Functional Transition Metal Silicates on Silica Gel:

Transition metal salt containing solution (0.5 g/ml) was added to silica gel (500 microns) and immobilization was attained by adding sodium silicate or potassium silicate (0.5 g/ml, alkali:silica=1:1) solution. The unbound substances were washed extensively with distilled or deionized water and the functional transition metal silicate immobilized silica gel was obtained after drying at 100° C.

Immobilization of Functional Transition Metal Silicates on Quartz Sand:

Quartz sand of various sizes were washed thoroughly with light acid (0.1% HCl, or H₂SO₄) later after removing of acidic traces, the transition metal salt containing solution was added and dried at room temperature or in a oven, to obtain, more content of transition metal layer impregnated on sand particle. Later to the dried metal salt impregnated sand, the solution of sodium silicates or potassium (sodium to silica ratio=1:1) was mixed thoroughly to obtain, immobilized functional transition metal silicates at 2-3 pH. The unbound, non-impregnated or non-immobilized metal or other substances were washed extensively with distilled or deionized water, and the resultant material was dried. The immobilized functional transition metal silicate content on quartz sand was achieved up to 0.1-1.5 percent (w/w) based on number of coatings.

Immobilization of Functional Transition Metal Silicates by Incorporating in to Vinyl Ester, or Bisphenol or Isopthalic Resins

As previously described silver, copper, zinc, zirconium and manganese salts (such as chlorides, nitrates, sulphates) were added to solution of sodium silicate or potassium silicates to obtain functional transition metal silicates at acidic reaction conditions (pH 2) and these obtained functional transition metal silicates were mixed with resins such as vinyl ester, or bisphenol or isopthalic resins, without metallic catalysts (such as cobalt octate), and were allowed to polymerize after heating at 70° C. to 90° C. Later these materials were powdered to obtain desired particle size. Later these materials were powdered to obtain desired particle size. 5-20% (w/v) of functional transition metal silicates were incorporated in to resins.

The immobilized functional transition metal silicates of desired particle size (in microns) were obtained by grinding and or by passing through required size mesh.

Functional Transition Metal Silicate Containing Resin Coating on Solid Matrix materials such as Quartz Sand:

Functional transition metal silicates (silver silicate, cupric silicate, zinc silicate, zirconium silicate and manganese silicate) produced at acidic pH reaction conditions were mixed either with vinyl ester or bisphenol or isopthalic food grade resins at various doses ranging from 0.5:1 to 4:1 (w/v). This functional transition metal silicate containing resin was coated on solid matrix materials such as quartz sand by vigorously mixing. The resin-coated quartz sand was dried without addition of any catalyst or accelerators at 70° C. to 90° C. or by keeping at room temperature for a week, for polymerization.

Amount of immobilized functional transition metal silicate on a matrix varies based on initial concentration of transition metal salt, soluble silica, the reaction time, particle size and type of matrix, and mode of immobilization such as physical or chemical. These immobilizations in present invention can be classified as physical or chemical or incorporating directly into resins or coating of functional transition metal silicate containing resins on solid matrix like quartz sand.

The chemical immobilization means that transition metal salt solution reacts or transition metal content chemically binds to the material selected, such as activated alumina, agropolymer and silica gel. Activated alumina, as it is amphoteric, passes the electron to charged copper. Agropolymers contain transition metal binding reactive sites and can absorb significant amount of transition metal on to them.

Physical immobilization of functional transition metal silicates was done on cellulose, quartz sand, and incorporating into resins.

The immobilized functional transition metal silicates have extensive industrial applications for decontamination disinfection, and in other various fields. The wide application of the said functional transition metal silicates is an important aspect of the invention.

Accordingly the invention pertains to a method of producing immobilized functional transition metal silicates using activated alumina, aluminum oxide, cellulose, resins, quartz sand, functional transition metal silicate incorporated resins and functional transition metal silicate containing resin coatings on solid matrix like quartz sand. Flow diagram of manufacturing process of immobilized functional transition metal silicates

In the embodiment of present invention, a method of decontamination of toxic metals, like arsenic, mercury etc., and disinfection of microbes such as fungi, bacteria, viruses, and protozoa by functional transition metal silicates is described.

This invention describes immobilization of functional transition metal silicates, in three ways such as:

-   -   1. Immobilization on substances like activated alumina,         aluminium oxide, cellulose, vinyl ester resin, bisphenol resin,         isopthalic food grade resins, quartz sand, and silica gel.     -   2. Incorporation of functional transition metal silicates in to         resins such as vinyl ester resin or bisphenol resin or         isopthalic food grade resins and later polymerizing with these         resins.     -   3. Coating of functional transition metal silicates containing         resins on solid matrix like quartz sand.

This invention relates to effective utilization of immobilized functional transition metal silicates.

Although many methods are known for decontamination and disinfection using metals, but integrated methods, were not developed for both metal, chemical decontamination, and or microbial disinfection. Present method offers and integrated method of decontamination and disinfection of drinking water and other polluted water, at cheaper cost and in an effective way.

BRIEF DESCRIPTION OF THE STRUCTURAL DETAILS OF THE FUNCTIONAL TRANSITION METAL SILICATES ARE ENCLOSED IN THE ACCOMPANYING INFORMATION

FIG. 1-A: Composition analysis of cupric silicate (synthesized at acidic reaction conditions) using EDAX attached to SEM (Scanning Electron Microscope).

FIG. 1-B: ESR (Electron spin resonance) spectrometer analysis of cupric silicate (synthesized at acidic reaction conditions).

FIG. 1-C: XRD (X-ray diffraction) pattern of cupric silicate (synthesized at acidic reaction conditions).

FIG. 2-A: Composition analysis of cupric silicate (synthesized at acidic reaction conditions and at high temperature: 70° C. to 90° C.) using EDAX attached to SEM (Scanning Electron Microscope).

FIG. 2-B: ESR (Electron spin resonance) spectrometer analysis of cupric silicate (synthesized at acidic reaction conditions and at higher temperature: 70° C. to 90° C.).

FIG. 2-C: XRD (X-ray diffraction) pattern of cupric silicate (synthesized at acidic reaction conditions and at higher temperature: 70° C. to 90° C.).

FIG. 3-A: Composition analysis of cupric silicate (synthesized at neutral (pH 6-7) reaction conditions) using EDAX attached to SEM (Scanning Electron Microscope).

FIG. 3-B: ESR (Electron spin resonance) spectrometer analysis of cupric silicate (synthesized at neutral (pH 6-7) reaction conditions).

FIG. 3-C: XRD (X-ray diffraction) pattern of cupric silicate (synthesized at neutral (pH 6-7) reaction conditions).

FIG. 4-A: Composition analysis of cupric silicate (synthesized at basic (pH 10-11) reaction conditions) using EDAX attached to SEM (Scanning Electron Microscope).

FIG. 4-B: ESR (Electron spin resonance) spectrometer analysis of cupric silicate (synthesized at basic ( pH 10-1 1)reaction conditions).

FIG. 4-C: XRD (X-ray diffraction) pattern of cupric silicate (synthesized at basic (pH 10-11) reaction conditions).

FIG. 5-A: Composition analysis of cupric silicate (synthesized at extreme acidic (below pH 2) reaction conditions by addition of 10 ml of 36% HCl and at higher temperature: 70° C. to 90° C.) using EDAX attached to SEM (Scanning Electron Microscope).

FIG. 5-B: ESR (Electron spin resonance) spectrometer analysis of cupric silicate (synthesized at extreme acidic (below pH 2) reaction conditions by addition of 10 ml of 36% HCl and at higher temperature: 70° C. to 90° C.).

FIG. 5-C: XRD (X-ray diffraction) pattern of cupric silicate (synthesized at extreme acidic (below pH 2) reaction conditions by addition of 10 ml of 36% HCl and at higher temperature: 70° C. to 90° C.).

FIG. 6-A: Composition analysis of cupric silicate (synthesized at extreme acidic(below pH 2) reaction conditions by addition of 20 ml of 36% HCl and at higher temperature: 70° C. to 90° C.) using EDAX attached to SEM (Scanning Electron Microscope).

FIG. 6-B: ESR (Electron spin resonance) spectrometer analysis of cupric silicate (synthesized at extreme acidic (below pH 2) reaction conditions by addition of 20 ml of 36% HCl and at higher temperature: 70° C. to 90° C.).

FIG. 6-C: XRD (X-ray diffraction) pattern of cupric silicate (synthesized at extreme acidic (below pH 2) reaction conditions by addition of 20 ml of 36% HCl and at higher temperature: 70° C. to 90° C.).

FIG. 7-A: Composition analysis of zinc silicate (synthesized at neutral (pH 6-7) reaction conditions) using EDAX attached to SEM (Scanning Electron Microscope).

FIG. 7-B: ESR (Electron spin resonance) spectrometer analysis of zinc silicate (synthesized at neutral (pH 6-7) reaction conditions).

FIG. 7-C: XRD (X-ray diffraction) pattern of zinc silicate (synthesized at neutral (pH 6-7) reaction conditions).

FIG. 8-A: Composition analysis of zinc silicate (synthesized at extreme acidic reaction conditions (below pH 2) and at higher temperature: 70° C. to 90° C.) using EDAX attached to SEM (Scanning Electron Microscope).

FIG. 8-B: ESR (Electron spin resonance) spectrometer analysis of zinc silicate (synthesized at extreme acidic reaction conditions (below pH 2) and at higher temperature: 70° C. to 90° C.).

FIG. 8-C: XRD (X-ray diffraction) pattern of zinc silicate (synthesized at extreme acidic reaction conditions (below pH 2) and at higher temperature: 70° C. to 90° C.).

FIG. 9-A: Composition analysis of silver silicate (synthesized at neutral (pH 6-7) reaction conditions) using EDAX attached to SEM (Scanning Electron Microscope).

FIG. 9-B: ESR (Electron spin resonance) spectrometer analysis of silver silicate (synthesized at neutral (pH 6-7) reaction conditions).

FIG. 9-C: XRD (X-ray diffraction) pattern of silver silicate (synthesized at neutral (pH 6-7) reaction conditions).

FIG. 10-A: Composition analysis of silver silicate (synthesized at acidic (pH 2) reaction condition and at higher temperature: 70° C. to 90° C.) using EDAX attached to SEM (Scanning Electron Microscope).

FIG. 10-B: ESR (Electron spin resonance) spectrometer analysis of silver silicate (synthesized at acidic reaction conditions (pH 2) and at higher temperature: 70° C. to 90° C.).

FIG. 10-C: XRD (X-ray diffraction) pattern of silver silicate (synthesized at acidic reaction conditions (pH 2) and at higher temperature: 70° C. to 90° C.).

FIG. 11-A: Composition analysis of manganese silicate (synthesized at neutral (pH 6-7) reaction conditions) using EDAX attached to SEM (Scanning Electron Microscope).

FIG. 11-B: ESR (Electron spin resonance) spectrometer analysis of manganese silicate (synthesized at neutral (pH 6-7) reaction conditions).

FIG. 11-C: XRD (X-ray diffraction) pattern of manganese silicate (synthesized at neutral (pH 6-7) reaction conditions).

FIG. 12-A: Composition analysis of manganese silicate (synthesized at extreme acidic reaction conditions (below pH 2) and at higher temperature: 70° C. to 90° C.) using EDAX attached to SEM (Scanning Electron Microscope).

FIG. 12-B: ESR (Electron spin resonance) spectrometer analysis of manganese silicate (synthesized at extreme acidic reaction conditions (below pH 2) and at higher temperature: 70° C. to 90° C.).

FIG. 12-C: XRD (X-ray diffraction) pattern of manganese silicate (synthesized at extreme acidic reaction conditions (below pH 2) and at higher temperature: 70° C. to 90° C.).

FIG. 13-A: Composition analysis of zirconium silicate (synthesized at neutral (pH 6-7) reaction conditions) using EDAX attached to SEM (Scanning Electron Microscope.

FIG. 13-B: ESR (Electron spin resonance) spectrometer analysis of zirconium silicate (synthesized at neutral (pH 6-7) reaction conditions).

FIG. 13-C: XRD (X-ray diffraction) pattern of zirconium silicate (synthesized at neutral (pH 6-7) reaction conditions).

FIG. 14-A: Composition analysis of zirconium silicate (synthesized at extreme acidic reaction conditions (below pH 2) and at higher temperature: 70° C. to 90° C.) using EDAX attached to SEM (Scanning Electron Microscope).

FIG. 14-B: ESR (Electron spin resonance) spectrometer analysis of zirconium silicate (synthesized at extreme acidic reaction conditions (below pH 2) and at higher temperature: 70° C to 90° C.).

FIG. 14-C: XRD (X-ray diffraction) pattern of zirconium silicate (synthesized at extreme acidic reaction conditions (below pH 2) and at higher temperature: 70° C. to 90° C.).

*The functional transition metal silicates were analyzed by SEM/EDAX (ESEM, XL-30), ESR (JEOL, JES-FA-200), AND XRD (PHLIPS, PW-1830) to understand the composition, structure, etc., details.

Now applicant provide the following specific description by way of examples and illustrations of the invention and this should not be construed to limit the scope of the invention in any manner.

Synthesis of Cupric Silicates

Synthesis of cupric silicate will be described in detail with the following illustrations

1. Synthesis of Cupric Silicate at Acidic Reaction Conditions:

10 ml of sodium silicate solution (0.5 g/ml) having 2:1 silicate to sodium ratio was added to 100 ml of cupric chloride solution (Cucl₂ 2H₂O, 0.5 g/ml). The reaction condition is acidic. The resultant precipitate obtained after removal of supernatant was dried after thoroughly washing with distilled or deionized water.

The silicate to copper ratio was 1: 5.15 as revealed from analysis of this cupric silicate by using EDAX attached to SEM (Scanning Electron Microscope) and further confirmed by analyzing with AAS or ICP-AES (FIG. 1-A).

This Cupric silicate when subjected to analysis by electron spin resonance spectrometer resulted in characteristic g values of the peaks, which were presented below (as shown in FIG. 1-B and Table 1).

A) 4.32481 B) 2.55205 C) 2.31749 D) 2.08807 E) 2.04673

This Cupric silicate when subjected to X-ray Diffraction analysis resulted in 8 peaks as evidenced in FIG. 4, which shows 3 significant peaks, and peak height, (counts/s) and Angle (° 2 theta) of these 3 peaks were presented below (as shown in FIG. 1-C, and Table 1).

1) 2128.25 and 16.28197 2) 1593.74 and 32.29018 3) 1470.73 and 39.79307

This cupric silicate decontaminated arsenic up to 42.5%, when 500 mg of this material was treated by mixing with 1 liter of 2.5 ppm arsenic solution prepared from sodium arsenate (Table 1).

This cupric silicate disinfected 2.72x10 5 coliform bacteria from drinking water, when 10 mg of cupric silicate was added to 1 liter of coliform contaminated drinking water (Table 1).

This cupric silicate inhibited the growth of gram positive and gram-negative bacteria such as E. Coli, Staphylococcus aureus, Pseudomonas aeruginosa, and Bacillus subtilis when cupric silicate (0.25%) was mixed with bacterial growth media (Table 3).

Even at a concentration of 0.06% and 0.125% of this cupric silicate in growth media inhibited the growth of E. coli (Table 4).

This Cupric silicate inhibited fungal growth of a) Sclerotium rolfsii b) Rhizoctonia solani c) Fusarium oxysporium d) Pyricularia oryzae (Table 6), up to 32.93, 73.2, 76.8, and 100% respectively, with 0.25% material concentration mixed in growth media of fungus (Table 6).

Viral disinfection nature of this Cupric silicate was analyzed using Bacteriophages and this cupric silicate disinfected the viruses.

The phages used in this study, their isoelectric points (pl) and their hosts are as follows: MS2 (ATCC 155597-B1), pl 3.9, Escherichia coli C-3000 (ATCC 15997); NX-174 (ATCC 13706-B1) pl6.6, E. Coli (ATCC 13706); and PRD-1, pl 4.2, Salmonella typhimurium (ATCC 19585). Phages were assayed as plaque-forming units (PFU) using their respective hosts and a soft-agar overlay described by Snustad, S. A., and D. S. Dean (Genetic experiments with bacterial viruses, 1971, W. H. Freeman and Co., San Francisco).

Batch Absorption Studies:

Three hundred milligrams of the cupric silicate was aseptically weighed and placed into each of three sterile 50 ml conical bottom centrifuge tube. Aliquots as the bacteriophage stocks were added to 100 ml of sterile deionized water (DI, Ph 7.8-8.4) to achieve final concentration of approximately 10⁵ pfu/ml. Fifteen milliliter of the seeded DI was added to each of the three tubes containing the material. A control tube containing seeded DI and no material was also prepared. The tubes were sealed then placed on a rotary shaker (Red Rotor PR70/75, Hoofer Scientific, CA) for 10 min at medium speed (0.8 rps). The tubes were removed and centrifuged at 3000g for 5 min. Aliquots of the supernatant and the control seeded DI were removed, serially diluted, and assayed for the respective Bacteriophages as described above.

Cupric silicate decontaminated about 90% Bacteriophage viruses such as MS-2, ØX174 and PRD-1 (as shown in table 7).

This cupric silicate exhibited chemical pollutant decontamination property when this cupric silicate (500 mg) was added to trihalomethanes (such as chloroform, 1,1,1, trichloroethane, tetrachloroethylene, trichloroethylene, bromodichloroethane, dibromochloroethane, tetrachloroethylene, bromoform, 1,2, dichlor-3-bromopropane) dissolved in water. After thorough mixing of cupric silicate with 8.950 ppm trihalomethanes containing water, the supernatant analysis after precipitation of cupric silicate revealed that cupric silicate decontaminated trihalomethanes. Cupric silicate decontaminated 5.4 ppm of trihalomethanes out of 8.95 ppm trihallomethanes as shown in (Table 8).

2. Synthesis of Cupric Silicate at Acidic Reaction Conditions and at Higher Temperature (70° C. to 90° C.):

50 ml of sodium silicate solution (0.5 g/ml) having 1:1 silicate to sodium ratio was added to 100 ml cupric chloride solution (0.5 g/ml). After thorough mixing the reactants were heated up to 70° C. to 90° C. and kept overnight for 12 hours. The precipitate obtained was extensively washed with distilled or deionized water and dried in oven at 100 ° C.

The silicate to copper ratio was 1: 0.78, as revealed from analysis of cupric silicate by using EDAX attached to scanning electron microscope and further confirmed by analyzing with AAS or ICP-AES (FIG. 2-A).

This Cupric silicate when subjected to analysis by electron spin resonance spectrometer resulted in characteristic g values of the peaks, which were presented below (as shown in FIG. 2-B, and Table 1).

A) 2.23480 B) 2.06456

This Cupric silicate when subjected to X-ray Diffraction analysis resulted in 7peaks as evidenced in FIG. 6, which shows 3 significant peaks, and peak height, (counts/s) and Angle (°2 theta) of these 3 peaks, which were presented below (as shown in FIG. 2-C and Table 1).

1) 835.63 and 16.20057

2) 706.74 and 32.23910

3) 502.52 and 39.57159

This Cupric silicate decontaminated arsenic up to 55.8%, when 500 mg of this material was treated by mixing with 1 liter of 2.5 ppm arsenic solution prepared from sodium arsenate (as shown in Table 1).

This cupric silicate disinfected 2.72×10⁵ coliform bacteria from drinking water, when 10 mg of cupric silicate was added to 1 liter of coliform contaminated drinking water (Table1).

3. Synthesis of Cupric Silicate at Neutral Reaction Conditions (pH: 6-7):

Appropriate amount of sodium silicate solution (0.5 g/ml) having 1:1 silicate to sodium ratio was added to O0mil of cupric chloride (0.5 g/ml) solution to obtain neutral pH condition. The resultant precipitate containing cupric silicate was obtained after removal of supernatant and dried after thoroughly washing with distilled or deionized water.

The silicate to copper ratio was 1:1, as revealed from analysis of this cupric silicate by using EDAX attached to scanning electron microscope and by further confirmed by analyzing with AAS or ICP-AES (FIG. 3-A).

This cupric silicate when subjected to analysis by electron spin resonance spectrometer resulted in characteristic g values of the peaks, which were presented below (as shown in FIG. 3-B, and Table 1).

A) 3.10383 B) 2.36522 C) 2.0467 D) 1.21887 E) 0.96688

This cupric silicate when subjected to X-ray diffraction analysis resulted in 6 peaks as evidenced in FIG. 3-C, which shows 3 significant peaks, and peak height, (counts/s) and angle (°2 theta) of these 3 peaks were presented below (as shown in FIG. 3-C and Table 1).

1. 940.90 and 16.19577

2. 764.43 and 32.29276

3. 694.85 and 39.77809

This cupric silicate decontaminated arsenic up to 27.7%, when 500 mg of this material was treated by mixing with 1 liter of 2.5 ppm arsenic solution prepared from sodium arsenate (Table 1).

This cupric silicate disinfected 2.72×10⁵ coliform bacteria from drinking water, when 10 mg of cupric silicate was added to 1 liter of coliform contaminated drinking water (Table 1).

This cupric silicate inhibited fungal growth of a) Sclerotium rolfsii b) Rhizoctonia solani c) Fusarium oxysporium d) Pyricularia oryzae (Table 6), up to 24.7, 59.0, 68.3 and 88.5% respectively, with 0.25% material concentration present in growth media of fungus.

4. Synthesis of Cupric Silicate at Basic Reaction Conditions (pH: 10-11):

Required amount of sodium silicate solution (0.5 g/ml) having 1:1 silicate to sodium ratio was added to 100 ml of cupric chloride solution (0.5 g/ml) to obtain basic pH condition (10-11 pH). The resultant precipitate was obtained after removal of supernatant and dried after thoroughly washing with distilled or deionized water.

The silicate to copper ratio was 1:0.83 as revealed from analysis of this cupric silicate by using EDAX attached to scanning electron microscope and further confirmed by analyzing with AAS or ICP-AES (FIG. 4-A).

This cupric silicate when subjected to analysis by electron spin resonance spectrometer resulted in characteristic g values of the peaks, which were presented below (as shown in FIG. 4-B, and Table 1).

A) 3.71806 B) 3.23001 C) 2.61681

This cupric silicate when subjected to X-ray diffraction analysis resulted in 3 peaks as evidenced in FIG. 4-C, which shows 1 significant peak, and peak height, (counts/s) and angle (° 2 theta) of this peak is presented below (as shown in FIG. 4-C and Table 1).

1) 152.74 and 26.64983

This cupric silicate decontaminated arsenic up to 8%, when 500 mg of this material was treated by mixing with 1 liter of 2.5 ppm arsenic solution prepared from sodium arsenate (Table 1).

This cupric silicate disinfected 21.69% only out of 2.72×10⁵ coliform bacteria from drinking water, when 250 mg of cupric silicate was added to 1 liter of coliform contaminated drinking water (Table 1).

5. Synthesis of Cupric Silicate Obtained by Addition of 10 ml of 36% HCl into Reaction Medium at Extreme Acidic Reaction Conditions (below 2 pH):

10 ml of 36% analytical grade HCl was added to 100 ml of cupric chloride (0.5 g/ll) solution. To these acidic cupric chloride solutions, 50 ml of sodium silicate solution (0.5 g/ml) having 1:1 silicate to sodium ratio was added. After thorough mixing, the reactants were heated up to 70° C. to 90° C. and kept overnight for 12 hours. The precipitate obtained was extensively washed with distilled or deionized water and dried in oven at 100 0 C. The silicate to copper ratio was 1:0.53 as revealed from analysis of this cupric silicate by using EDAX attached to scanning electron microscope and further confirmed by analyzing with AAS or ICP-AES (FIG. 5-A).

This cupric silicate when subjected to analysis by electron spin resonance spectrometer resulted in characteristic g values of the peaks, which were presented below (as shown in FIG. 5-B and Table 1).

A) 2.18421 B) 2.06874 C) 1.21231

This cupric silicate when subjected to X-ray diffraction analysis resulted in 6 peaks as evidenced in FIG. 5-C, which shows 3 significant peaks, and peak height, (counts/s) and angle (° 2 theta) of these 3 peaks were presented below (as shown in FIG. 5-C, and Table 1).

1) 400.70 and 16.19872

2) 394.77 and 32.27956

3) 330.02 and 39.71761

This cupric silicate decontaminated arsenic up to 42%, when 500 mg of this material was treated by mixing with 1 liter of 2.5 ppm arsenic solution prepared from sodium arsenate (Table 1).

This cupric silicate disinfected 2.72×10⁵ coliform bacteria from drinking water, when 10 mg of cupric silicate was added to 1 liter of coliform contaminated drinking water (Table 1).

6. Synthesis of Cupric Silicate Obtained by Addition of 20 ml of 36% HCl into Reaction Medium at Extreme Acidic Reaction Conditions (below pH 2):

20 ml of 36% analytical grade HCl was added to 100 ml of cupric chloride (0.5 g/ml) solution. To these acidic cupric chloride solutions, 50 ml of sodium silicate solution (0.5 g/ml) having 1:1 silicate to sodium ratio was added. After thorough mixing the reactants were heated up to 70° C. to 90° C. and kept overnight for 12 hours. The precipitate obtained was extensively washed with distilled or deionized water and dried in oven at 100 ° C.

The silicate to copper ratio was 1: 0.34 as revealed from analysis of this cupric silicate by using EDAX attached to scanning electron microscope and further confirmed by analyzing with AAS or ICP-AES (FIG. 6-A).

This cupric silicate when subjected to analysis by electron spin resonance spectrometer resulted in characteristic g values of the peaks were presented below (as shown in FIG. 6-B, and Table 1).

A) 2.15561 B) 2.03614

This cupric silicate when subjected to X-ray diffraction analysis resulted in 7 peaks as evidenced in FIG. 6-C, which shows 3 significant peaks, and peak height, (counts/s) and angle (° 2 theta) of these 3 peaks were presented below (as shown in FIG. 6-C and Table 1).

1) 541.23 and16.26305

2) 414.21 and 32.36589

3) 365.45 and 39.85131

This cupric silicate decontaminated arsenic up to 27.7%, when 500 mg of this material was treated by mixing with 1 Liter of 2.5 ppm arsenic solution prepared from sodium arsenate (Table 1).

This cupric silicate disinfected 2.72×10⁵ coliform bacteria from drinking water, when 10 mg of cupric silicate was added to 1 liter of coliform contaminated drinking water (Table 1).

Synthesis of Zinc Silicates:

7) Synthesis of Zinc Silicates at Neutral Reaction Conditions (pH: 6-7):

Appropriate amount of sodium silicate solution (0.5 g/ml) having 2:1 silicate to sodium ratio was added to 100 ml of zinc chloride (ZnCl₂, 0.5 g/ml) solution to obtain neutral pH condition. The resultant precipitate containing zinc silicate was obtained after removal of supernatant and dried after thoroughly washing with distilled or deionized water.

The silicate to zinc ratio was 1:12.13 as revealed from analysis of this zinc silicate by using EDAX attached to scanning electron microscope and further confirmed by analyzing with AAS or ICP-AES (FIG. 7-A).

This zinc silicate when subjected to analysis by electron spin resonance spectrometer resulted in characteristic g values of the peaks, which were presented below (as shown in FIG. 7-B, and Table 2).

A) 5.49809 B) 4.55342 C) 2.54593 D) 2.10091 E) 2.05499

This zinc silicate when subjected to X-ray diffraction analysis resulted in 8 peaks as evidenced in FIG. 7-C, which shows 3 significant peaks and peak height, (counts/s) and Angle (° 2 theta) of these 3 peaks were presented below (as shown in FIG. 9 and Table 2).

1) 444.15 and 32.75904

2) 307.02 and 59.58455

3) 263.36 and 28.27636

This zinc silicate decontaminated arsenic up to 98.7%, when 1.0 gram of this material was treated by mixing with 1 Liter of 2.5 ppm arsenic solution prepared from sodium arsenate (Table 2).

This zinc silicate disinfected 96% out of 2.72×10⁵ coliform bacteria from drinking water, when 250 mg of zinc silicate was added to 1 liter of coliform contaminated drinking water (Table 2).

Zinc silicate at a concentration of 0.25% in the growth media exhibited bactericidal property by inhibiting the growth of Staphylococcus aureus (as shown in table 5).

8) Synthesis of Zinc Silicates at Extreme Acidic Reaction Conditions (Below 2 pH):

10 ml of 36% analytical grade HCl was added to 100 ml of zinc chloride solution (0.5 g/ml). 50 ml of sodium silicate solution (0.5 g/ml) having 2:1 silicate to sodium ratio was added to the HCl containing zinc chloride solution. After thorough mixing, the reactants were heated up to 70° C. to 90° C. and kept overnight for 12 hours. The resultant precipitate containing zinc silicate was obtained after removal of supernatant and dried after thoroughly washing with -distilled or deionized water.

The silicate to zinc ratio was 1:2.46 as revealed from analysis of this zinc silicate by using EDAX attached to scanning electron microscope and further confirmed by analyzing with AAS or ICP-AES (FIG. 8-A),

This Zinc silicate when subjected to analysis by electron spin resonance spectrometer resulted in characteristic g values of the peaks, which were presented below (as shown in FIG. 8-B, and Table 2).

A) 4.38410 B) 4.01910 C) 2.53191 D) 1.87886 E) 2.01793

This zinc silicate when subjected to X-ray Diffraction analysis resulted in 26 peaks as evidenced in FIG. 8-C, which shows 3 significant peaks and peak height, (counts/s) and angle (° 2 theta) of these 3peaks were presented below (as shown in FIG. 8-C and Table 2).

1) 2079.88 and 11.07467

2) 835.44 and 33.52527

3) 664.98 and 32.88120

This zinc silicate decontaminated arsenic up to 72.3%, when l.Ogram of this material was treated by mixing with 1 liter of 2.5 ppm arsenic solution prepared from sodium arsenate (Table 2).

This zinc silicate disinfected 99% out of 2.72×10⁵ coliform bacteria from drinking water, when 250 mg of zinc silicate was added to 1 liter of coliform contaminated drinking water (Table 2).

Synthesis of Silver Silicates:

9) Synthesis of Silver Silicates at Neutral Reaction Conditions (6-7 pH):

100 ml of silver nitrate (AgNO₃, 0.5 g/ml) solution was mixed with required amount of sodium silicate solution (1:1=sodium:silica, 0.5 g/ml) having 2:1 silica, transition metal ratio to attain neutral pH in the reaction. After addition, of reactants they were thoroughly mixed and the resultant precipitate was obtained by decanting the supernatant. The precipitate was washed extensively with distilled or deionized water and dried in oven at 100° C.

The silicate to silver ratio was 1:19.5 as revealed from analysis of this silver silicate by using EDAX attached to scanning electron microscope and further confirmed by analyzing with AAS or ICP-AES (FIG. 9-A).

This silver silicate when subjected to analysis by electron spin resonance spectrometer resulted in characteristic g values of the peaks, which were presented below (as shown in FIG. 9-B, and Table 2).

A) 4.36796 B) 2.37847 C) 3.95509 D) 2.04657

This silver silicate when subjected to X-ray diffraction analysis resulted in 19 peaks as evidenced in FIG. 9-C, which shows 3 significant peaks and peak height, (counts/s) and Angle (° 2 theta) of these 3peaks were presented below (as shown in FIG. 9-C and Table 2).

1) 3945.11 and 32.29885

2) 2421.27 and 46.27446

3) 1835.66 and 27.89129

This silver silicate decontaminated arsenic up to only 4.5%, when 1.0 gram of this material was treated by mixing with 1 liter of 2.5 ppm arsenic solution prepared from sodium arsenate (Table 2).

This silver silicate disinfected 2.72×10⁵ coliform bacteria from drinking water, when 5 mg of silver silicate was added to 1 liter of coliform contaminated drinking water (shown in Table 2).

10) Synthesis of Silver Silicates at Acidic Reaction Conditions (pH: 2):

8 ml of nitric acid solution (69-70%) was added to 50 ml of silver nitrate (0.5 g/ml) solution. Required amount of sodium silicate (1:1=sodium:silica, 0.5 g/ml) solution, 2:1 silica, transition metal ratio was added to this acidified silver nitrate solution to obtain 2 pH. After thorough mixing, the reactants were heated up to 70° C. to 90° C. and kept overnight for 12 hours. The resultant precipitate was washed extensively with distilled or deionized water and dried in oven at 100° C.

The silicate to silver ratio was 1:1.04 as revealed from analysis of this silver silicate by using EDAX attached to scanning electron microscope and further confirmed by analyzing with AAS or ICP-AES (FIG. 10-A).

This silver silicate when subjected to analysis by electron spin resonance spectrometer resulted in characteristic g values of the peaks, which were presented below (as shown in FIG. 10-B, and Table 2).

A) 4.37171 B) 4.04714 C) 1.98189

This silver silicate when subjected to X-ray diffraction analysis resulted in 19 peaks as evidenced in FIG. 10-C, which shows 3 significant peaks and peak height, (counts/s) and angle (° 2 theta) of these 3peaks were presented below (as shown in FIG. 10-C and Table 2).

1) 2217.87 and 29.33483

2) 684.55 and 47.68093

3) 674.27 and 42.31091

This silver silicate decontaminated arsenic up to 99.0%, when 1.0 gram of this material was treated by mixing with 1 Liter of 2.5 ppm arsenic solution prepared from sodium arsenate (Table 2).

This silver silicate disinfected 2.72×10⁵ coliform bacteria from drinking water, when 5 mg of silver silicate was added to 1 liter of coliform contaminated drinking water (Table 2).

Synthesis of Manganese Silicates:

11) Synthesis of Manganese Silicates at Neutral Reaction Conditions (pH: 6-7):

100 ml of Manganese chloride (Mncl₂ 4H₂O, 0.5 g/ml) solution was mixed with required amount of sodium silicate solution (1:1=sodium:silica, 0.5 g/ml) to obtain neutral pH (6-7) in the reaction medium. After addition, they were thoroughly mixed and the resultant precipitate was obtained by decanting the supernatant. The precipitate was washed extensively with distilled or deionized water and dried in oven at 100° C.

The silicate to manganese ratio was 1:1.94 as revealed from analysis of this manganese silicate by using EDAX attached to scanning electron microscope and further confirmed by analyzing with AAS or ICP-AES (FIG. 11-A).

This manganese silicate when subjected to analysis by electron spin resonance spectrometer resulted in characteristic g values of the peaks, which were presented below (as shown in FIG. 11-B, and Table 2).

A) 1.93412 B) 2.06655

This manganese silicate when subjected to X-ray diffraction analysis resulted in 5 peaks as evidenced in FIG. 11-C, which shows one significant peak and peak height, (counts/s), Angle (° 2 theta) of this single peak were presented below (as shown in FIG. 11-C and Table 2).

a) 148.04 and 30.65087

This manganese silicate decontaminated arsenic up to 12.4%, when 1.0 gram of this material was treated by mixing with 1 liter of 2.5 ppm arsenic solution prepared from sodium arsenate (Table 2).

This manganese silicate disinfected 51% out of 2.72×10⁵ coliform bacteria from drinking water, when 500 mg of manganese silicate was added to 1 liter of coliform contaminated drinking water (Table 2).

12) Synthesis of Manganese Silicates at Extreme Acidic Reaction Conditions (Below 2 pH):

10 ml of 36% HCl was added to 100 ml of manganese chloride solution (0.5 g/ml). Sodium silicate solution (1:1=sodium:silica, 0.5 g/ml,), 50 ml was added to acidified manganese chloride solution. After thorough mixing, the reactants were heated up to 70° C. to 90° C. and kept overnight for 12 hours. The resultant precipitate was washed extensively with distiller water or deionized water and dried in oven at 100° C.

The silicate to manganese ratio was 1:1:09 as revealed from analysis of this manganese silicate by using EDAX attached to scanning electron microscope and further confirmed by analyzing with AAS or ICP-AES (FIG. 12-A).

This manganese silicate when subjected to analysis by electron spin resonance spectrometer resulted in characteristic g values of the peaks, which were presented below (as shown in FIG. 12-B, and Table 2).

A) 4.34636B) 4.17458C) 2.18228D) 2.11243 E) 2.05491F) 1.999661

This manganese silicate when subjected to X-ray diffraction analysis resulted in one peak as evidenced in FIG. 12-C, which shows one significant peak and peak height (counts/s) and angle (° 2 theta) of this peak were presented below (as shown in FIG. 12-C and Table 2).

a) 32.88 and 24.65599

This manganese silicate decontaminated arsenic up to 10.3%, when 1.0 gram of this material was treated with 1 liter of 2.5 ppm arsenic solution prepared from sodium arsenate (Table 2).

This manganese silicate disinfected 58% out of 2.72×10⁵ coliform bacteria from drinking water, when 500 mg of manganese silicate was added to 1 liter of coliform contaminated drinking water (Table 2).

Synthesis of Zirconium Silicates:

13) Synthesis of Zirconium Silicates at Neutral Reaction Conditions (pH: 6-7)

To 100 ml of zirconium oxychloride solution (ZrOCl₂ 8H₂O, 0.5 g/ml), required amount of sodium silicate solution (1:1=sodium:silica, 0.5 g/ml) was added to obtain neutral pH. After addition, they were thoroughly mixed and the resultant precipitate was obtained by decanting the supernatant. The precipitate was washed extensively with distilled or deionized water and dried in oven at 100° C.

The silicate to zirconium ratio was 1:2.90 as revealed from analysis of this zirconium silicate by using EDAX attached to scanning electron microscope and further confirmed by analyzing with AAS or ICP-AES (FIG. 13-A).

This zirconium silicate when subjected to analysis by electron spin resonance spectrometer resulted in characteristic g values of the peaks, which were presented below (as shown in FIG. 13-B, and Table 2).

A) 4.42797B) 4.18272 C) 2.24547 D) 2.30425E) 2.18961F) 1.23086

This zirconium silicate when subjected to X-ray diffraction analysis resulted no peak as evidenced in FIG. 13-C.

This zirconium silicate decontaminated arsenic up to 28.9%, when 1.0 gram of this material was treated by mixing with 1 liter of 2.5 ppm arsenic solution prepared from sodium arsenate (Table 2).

This zirconium silicate disinfected 2% out of 2.72×10⁵ coliform bacteria from drinking water, when 250 mg of zirconium silicate was added to 1 liter of coliform contaminated drinking water (Table 2).

14) Synthesis of Zirconium Silicates at Extreme Acidic Reaction Conditions (Below 2 pH):

To 100 ml of zirconium oxychloride solution, 10 ml of 36% HCl and sodium silicate solution (1:1=sodium:silica, 0.5 g/ml) 50 ml were added and mixed well. After thorough mixing, the reactants were heated up to 70° C to 90° C. and kept overnight for 12 hours. The resultant precipitate was washed extensively with distilled or deionized water and dried in oven at 100° C.

The silicate to zirconium ratio was 1:0.77 as revealed from analysis of this zirconium silicate by using EDAX attached to scanning electron microscope and further confirmed by analyzing with AAS or ICP-AES (FIG. 14-A).

This zirconium silicate when subjected to analysis by electron spin resonance spectrometer resulted in characteristic g values of the peaks, which were presented below (as shown in FIG. 14-B, and Table 2).

A) 4.37236 B) 2.82039C) 1.92596D) 1.21652E) 1.02930F) 0.93795

This zirconium silicate when subjected to X-ray diffraction analysis resulted in 1 peak as evidenced in FIG. 14-C, which shows one significant peak, and peak height (counts/s) and angle (° 2 theta) of this peak were presented below (as shown in FIG. 14-C and Table 2).

A) 84.80 and 10.89433

This zirconium silicate decontaminated arsenic up to 54.5%, when 1.0 gram of this material was treated by mixing with 1 liter of 2.5 ppm arsenic solution prepared from Sodium arsenate (Table 2).

This zirconium silicate disinfected 98% out of 2.72×10⁵ coliform bacteria from drinking water, when 250 mg of zirconium silicate was added to 1 liter of coliform contaminated drinking water (Table 2).

Now the present invention will be described in detail based on the experiments conducted with immobilized functional transition metal silicates.

15) Arsenic Decontamination of Immobilized Functional Transition Metal Silicates on Activated Alumina (Size: Above 1000 microns):

250 ml of Sodium arsenate solution (containing 2.12 ppm of arsenic) was passed through 10×1 cm column at a flow rate of 10 ml/min. The arsenic content present in treated solution was measured by using ICP-AES and or AAS.

As evidenced from Table 8 the immobilized functional transition metal silicates absorbed arsenic significantly.

Cupric silicate immobilized on activated alumina, decontaminated arsenic content 90.10%. Zinc silicate immobilized on activated alumina decontaminated arsenic content 91.98%. Manganese silicate immobilized on activated alumina decontaminated arsenic content 58.96%. Zirconium silicate immobilized on activated alumina decontaminated arsenic content 13.08%.

16) Arsenic Decontamination of Immobilized Functional Transition Metal Silicates on Different Sizes on Activated Alumina:

1000 ml of Sodium arsenate solution (containing 2.4 ppm of arsenic) was passed through 10×1 cm column at a flow rate of 10 mil/min. Different sizes of immobilized functional transition metal silicates on activated alumina granules (500 microns and 1000 microns size,) were tested. The arsenic content present in treated solution was measured by using ICP-AES and or AAS.

Cupric silicate, immobilized on activated alumina (500 microns) decontaminated arsenic up to 95.58% compared to 86.05% decontamination resulted in treatment with cupric silicate, immobilized on activated alumina of 1000 microns size (Table-10).

17) Arsenic Decontamination Property of Immobilized Functional Transition Metal Silicates on Agropolymers:

250 ml of sodium arsenate solution (containing 500 ppb of arsenic) was passed through 250 mg of cupric silicate immobilized on agropolymer containing column at a flow rate of 1 ml/min. The arsenic content present in treated solution was measured by using ICP-AES and or AAS.

As evidenced from Table 11 the immobilized functional transition metal silicates on agropolymers absorbed arsenic significantly.

Cupric silicate immobilized on agropolymer decontaminated 56.48% of arsenic content.

18) Decontamination Property of Functional Transition Metal Silicates by Physical Immobilization on Quartz Sand (250-500 microns Size):

Immobilized functional transition metal silicates were prepared by adding transition metal salt containing solution to quartz sand (250-500 microns size), later reacting with sodium silicate to obtain immobilized functional transition metal silicate on quartz sand. Excess unbound non-immobilized substances were removed after through washing with distilled or deionized water. 250 ml of sodium arsenate solution (containing 2.12 ppm of arsenic) was passed through 10×1 cm containing column at a flow rate of 10 ml/min. The arsenic content present in treated solution was measured by using ICP-AES and or AAS.

As evidenced from Table 12 the immobilized functional transition metal silicates coated on quartz sand absorbed arsenic significantly.

Cupric silicate, zinc silicate, manganese silicate, and zirconium silicate decontaminated arsenic 35%, 48.58%, 18.87%, and 8.1% respectively, compared to 1.88% arsenic decontamination by quartz sand (control).

19) Mercury Decontamination Property of Immobilized Functional Transition Metal Silicates on Activated Alumina and Agropolymer:

Immobilized functional transition metal silicates on activated alumina and agropolymer were reacted separately with mercury containing solutions (224.21 ppb mercuric content) in a batch mode of a liter solution at a dose of 1 mg/ml. These materials were mixed well for 1 hour in mercury containing solutions and mercuric content (ppb) after treatment was measured by using AAS (hydria attached to graphite furnace).

Immobilized functional transition metal silicates sequestered mercury from the solution to below detection limits (as shown in Table 13).

20) Protein Decontamination Property of Immobilized Functional Transition Metal Silicates:

100 ml of BSA solution (1 mg/ml BSA content), was passed through 2×1 cm column of immobilized functional transition metal silicates on agropolymer and the protein bound to the immobilized functional transition metal silicate was assayed by estimating protein content in treated solutions by Lowry method.

As indicated in Table 14 the immobilized functional transition metal silicates decontaminated proteins.

Silver silicate immobilized on agropolymer-absorbed 10 mg of BSA protein compared to 15.4 mg and 3 mg absorption by cupric silicate immobilized on agropolymer and zinc silicate immobilized on agropolymer respectively. Total reaction volume is 100 ml containing 100 mg BSA protein.

21) Pesticides Decontamination Nature of Functional Transition Metal Silicates Immobilized on Agropolymers:

A solution containing 10 ppm each of Endosulphan, Cypermethrin and Chlorpyriphos was passed through a column containing 1 gm of immobilized cupric silicate (on activated alumina and agropolymer) at a rate of 0.5 ml/min. Pesticide content in treated solution was estimated by G.C.-ECD/p FPD.

As shown in Table 15 cupric silicates immobilized on activated alumina and agropolymer decontaminated of pesticides such as Endosulphan, Cypermethrin, and Chlorpyriphos.

Cupric silicate immobilized on activated alumina decontaminated 59.7% Endosulphan, 62.4% Cypermethrin and 46.6% Chlorpyriphos respectively.

Cupric silicate immobilized on agropolymer decontaminated 61.7% Endosulphan, 83.4% Cypermethrin and 49.1% Chlorpyriphos respectively.

22) Bacterial (Coliform) Decontamination of Immobilized Functional Transition Metal Silicates on Activated Alumina:

Bacterial coliform (5×10⁵) containing 500 ml of water was passed through 10 cm length immobilized functional transition metal silicate on activated alumina column at a flow rate of 10 ml/min.

The decontamination was assayed by measuring bacterial colonies in a petriplate containing bacterial growth medium.

As evidenced from Table 16 the immobilized functional transition metal silicates decontaminated coliform significantly. Silver silicate, cupric silicate decontaminated coliform content up to 98%, and 83% respectively. Zinc silicate immobilized on activated alumina decontaminated coliform content up to 43%.

23) Bacterial Decontamination of Immobilized Functional Transition Metal Silicates on Agropolymers:

Bacterial coliform containing water was passed through 250 mg containing (functional transition metal silicates immobilized on agropolymer) column at a flow rate of 10 ml/min, and bacterial colonies in treated solution was assayed in a petriplate containing bacterial growth medium.

The results as shown in Table 17 indicates that immobilized functional transition metal silicates decontaminated coliform bacteria from water.

Cupric silicate immobilized on agropolymer decontaminated coliform bacteria (coliform concentration of treated water=4×10⁴/liter) 99%, 97.45% and 94.87% from 2000 ml, 2500 ml and 3000 ml of coliform containing water respectively. Whereas silver silicate immobilized on agropolymer decontaminated coliform up to 99% from 3000 ml coliform containing water. Zinc silicate immobilized on agropolymer decontaminated 61.90%, 14.28% and 4.76% coliform content from 1000 ml, 1500 ml and 2000 ml coliform contaminated water.

24) Bacterial Decontamination Property of Immobilized Functional Transition Metal Silicates on Aluminium Oxides, Cellulose:

Bacterial coliform containing water was passed through immobilized functional transition metal silicates on column mode. The immobilized functional transition metal silicates on aluminium oxide, cellulose were tested for their bacterial decontamination property. The coliform containing water (460 colonies/ml) was passed through their immobilized functional transition metal silicates columns at a flow rate of 5 ml/min.

The decontamination was assayed by measuring bacterial colonies in a petriplate containing bacterial growth medium.

The results as shown in Table 18 indicates that immobilized functional transition metal silicates decontaminated coliform bacteria from water.

Cupric silicate immobilized on aluminium oxide (1 gm filled in a column) decontaminated coliform up to 93.47% from 250 ml of coliform (1.15×10⁵) containing water cupric silicate immobilized on cellulose (0.97 gm filled in a column) decontaminated coliform up to 93.71% from 250 ml of coliform (1.38×10⁵) containing water.

25) Bacterial Decontamination Property of Immobilized Functional Transition Metal Silicates Coated on Quartz Sand:

Coliform containing 500 ml water was passed through 10×1 cm column of functional transition metal silicates coated on quartz sand at a flow rate of 10 ml/min.

The decontamination was assayed by measuring bacterial colonies in a petriplate containing bacterial growth medium.

Functional transition metal silicates immobilized on quartz sand decontaminated coliform bacteria. Cupric silicate immobilized on quartz sand decontaminated 83% compared to 34% decontamination by zinc silicate immobilized on quartz sand. Manganese silicate immobilized on quartz sand and zirconium silicate immobilized on quartz sand decontaminated coliform up to 5% and 6% respectively (Table 19).

26) Decontamination of Fungus (Aspergillus Species) from a Long Time (6 Months) Stored Water by Using Immobilized Functional Transition Metal Silicates:

Commercial available packaged drinking water was stored for 6 months, by allowing for development of microbial contaminants like fungus. After observing the contamination of fungus in the stored water present study was conducted to determine the fungal decontamination property of immobilized functional transition metal silicates. One liter of fungal contaminated water was passed through 2×1 cms. column of cupric silicate immobilized on agropolymer at a flow rate of 10 ml/min. Fungal presence was screened by placing the treated and untreated solutions on petriplates containing fungal growth medium.

Cupric silicate immobilized on agropolymer decontaminated fungus (Aspergillus species) from stored drinking water (Table 20).

27) Protozoan (Cryptosporidium parvum) Decontamination Property of Immobilized Functional Transition Metal Silicates:

One gram of the cupric silicate immobilized on agropolymers was aseptically weighed and placed into 10×1-cm glass columns. The bottom of the column contained glass wool to prevent the material from flowing through the column. The columns were gently tapped before and after wetting to assure uniform packing of the material. Three liters of deionized water was passed through the columns using a master flex L/S computerized drive pump (Cole-Palrer Instrument Co., Barrington, Ill., USA) at a flow rate of 15 ml/min to assure rinsing of the material. One milliliter of the cryptosporidium parvum stock (2×10⁷) was added to 200 ml of sterile deionized water (DI, pH.8-8.4). The seeded deionized water was then passed through the column using the above pump at a flow rate of 5 ml/min fractions of the column influent and effluent were collected after the passage of 20, 50 and 80 ml of seeded deionized water. The oocysts in the samples were enumerated by Immuno Florescent Assay (IFA). Briefly, the samples were filtered through a Sartorius cellulose acetate membrane filter and stained with FITC-labeled anti-Cryptosporidium monoclonal antibody (Crypt-o-Glow, waterborne, Inc New Orleans, La.). Filters were then dehydrated with and ethanol series (20, 40, 80, 90%) and viewed by epifluorescence microscopy. The oocysts were counted and the titer for each sample was calculated (Table 21).

Cupric silicate immobilized on agropolymer decontaminated Cryptosporidium parvum significantly (Table 21).

-   -   a. Viral decontamination property of immobilized functional         transition metal silicates.     -   b. E. coli o157:h7 (atcc 110195-b1) decontamination property of         immobilized functional transition metal silicates.

The following procedure was followed to assay the viral decontamination and bacterial decontamination property.

Viral Stock Preparation:

Polio Lsc 1 viral stock preparation was performed according to the methods of Berg Etal., (1984). Tissue culture flasks (T-182) were seeded with trypsiniazed Buffalo Green Monkey (BGM) cells and Minimum Essential Media (MEM, Cellgro®, Mediatech Inc., Cat#10010179) containing earl's salts, L-glutamine, 100u Penicillin G, 100 u Streptomycin, 0.25 μg/ml Amphotericin B, 100 mm HEPES, and 10% Fetal Bovine Serum (FBS). The flasks were incubated in a 36° C. incubator for 48 hours to allow the development of the continuous monolayer of cells. The flasks were then prepared for viral inoculation by rinsing the monolayer twice with Phosphate Buffered Saline (PBS) Aliquots of the Poliovirus Lsc 1 (ATCC VR-59) viral stocks were inoculated into the T-182 flasks containing continuous monolayer. The viral aliquots were allowed to incubate into the cell monolayer for 40 min. Following incubation; 35 ml of MEM containing earl's salts L-glutamine, 100 u penicillin G, 100 u Sterptomysin, 0.25 μg/ml Amphotericin B, and 100 mm HEPES was added to each of the flasks. The flasks were incubated at 36° C. for 36 hours. At this time >90+ of the monolayer exhibited significant Cyptopathic Effects (CPE). The flasks were then freeze-thawed (2×), and centrifuge at 10,000 g for 20 min. The supernatant was then collected; aliquoted, titrated, and stored at 70° C. till use.

Rotavirus preparation was conducted according to the procedure described by Smith and Gerba, (1982). Briefly, tissue culture flasks (T-182) were seeded with trypsiniazed MA-104 (ATCC Crl-2378) cells and Minimum Essential Media (MEM, Cellgro, Mediatech Inc., Cat #10010179) containing earl's salts, L-glutamine, 100 u Penicillin G, 100 u Streptomycin, 0.25 μg/ml Amphotericin B, 100 mm, HEPES, and 10% Fetal Bovine Serum (FBS). The flasks were incubated in a 36° C. incubator for 48 hours to allow the development of the continuous monolayer of cells. The flasks were then prepared for viral inoculation by rinsing the monolayer twice with Phosphate Buffered Saline (PBS). Aliquots of the Rotavirus SA 11 (ATCC VR-899) viral stocks were inoculated into the T-182 flasks containing continuous monolayer. The viral aliquots were allowed to incubate onto the cell monolayer for 40 min. Following incubation, 35 ml of MEM containing earl's salts, L-glutamine, 100 u Penicillin G, 100 u Streptomycin, 0.25 μg/ml. Amphotericin B, 5 mg/l Trypsin, and 100 mm HEPES was added to each of the flasks. The flasks were incubated at 36° C. for 6-8 days. At this time >90+ of the monolayer exhibited significant Cytopathic Effects (CPE). The flasks were then freeze-thawed (2×), and centrifuged at 10,000 g for 20 min. The supernatant was then collected, aliquoted, titrated, and stored at 70° C. till use.

Viral Enumeration:

Poliovirus 1 (Lsc1) was grown and assayed as pfu on Buffalo Green Monkey Kidney (BGM) cells by an agar overlay methos (Berg et al., 1984). Briefly, the samples were received frozen and thawed slowly to 4° C. Aliquots were inoculated onto recently passed (2-3 days) continuous monolayers of BGM cells. Monolayers in T-25 flasks received 1.0 ml inoculum, T-75 received 3.0 ml and T-182 received 6.0 ml. The influent samples were diluted ten fold in sterile PBS and 1.0 ml aliquots of the dilutions were inoculated onto monolayers in T-25 flasks. The samples were allowed to incubate for 40 min on the monolayers. 2× eMEM containing 8% FBS and 0.1% Neutral Red was mixed with equal volume of sterile molten 2.2% Bacto Agar (Becton Dickinson, Sparks Md.). The media was then added to each of the inoculated flasks, and the agar was allowed to solidify onto the monolayers. The flasks were then incubated at 36° C. for 2-5 days to allow plaque development and enumeration. The results of this assay are reported in Table-20.

Rotavirus SA 11 was assayed as most probable number on MA-104 cells. Briefly, aliquots of the received samples were inoculated onto recently passed (2-3 days) continuous monolayers of MA-104 cells. Prior to inoculation the monolayers in the flasks were rinsed twice with sterilse PBS. Monolayers in T-25 flasks received 1.0 ml inoculum, T-75 received 3.0 ml, and T-182 received 6.0 ml. The influent samples were monolayers diluted ten fold in sterile PBS and 1.0 ml aliquots of the dilutions were inoculated onto monolayers in T-25 flasks. All inoculums were adjusted to 5 mg/ltr trypsin and they were allowed to incubate onto the monolayer for 40 min. Following incubation, eMEM, L-glutamine, 100 u Penicillin G, 100 u Streptomycin, 0.25 μg/ml. Amphotercin B, 5 mg/ltr Trypsin, and 100 mm HEPES was added to each of the inoculated flasks. The flasks were then incubated at 36° C. for 7-10, 2-5 days to allow CPE development. The results of the assay are reported in Table-20.

Bacterial Cultures and Enumeration:

E. Coli O157: H7 (ATCC 110195-B1) was sub-cultured on tryptic soy agfar (Dicco Laboratories, Detroit, Mich.). For all experiments, inocula were prepared from cultures grown at 37° C. in tryptic soy both (TSB; Difco) for 18 to 24 hrs. Bacteria were enumerated by spread plating on tryptic soy agar (TSA) and incubating for 18-24 hours at 37° C.

Column Adsorption Studies:

Immobilized cupric silicate on agropolymer and immobilized cupric silicate on activated alumina (500 micron size) were aspectically weighed and placed into 10×1 cm glass columns. The bottom of the column contained glass wool to prevent the material from flowing through the column. The columns were gently tapped before and after wetting to assure uniform packing of the material. Three liters of DI was passed through the columns using Mate flex L/S computerized drive pump (Cole-Palrer Instrument Co., Barrington. Ill. USA) at a flow rate of 15 ml/min to assure rinsing of the material. Aliquots of the Rotavirus viral stock were added to 250 ml of sterile deionized water (DI, pH 7.8-8.4) to achieve final concentration of approximately 10⁶-pfu/ml. The seeded deionized water was then passed through the column using the above pump at a flow rate of 5 ml/min. Fractions of the column influent and effluent were collected after the passage of 50, 100, and 200 ml of seeded DI Following, aliquots of the Polio 1 viral stock and E. Coli O157:H7 overnight culture were added to another 250 ml of sterile deionized water (DI, pH7.8-8.4) to achieve final concentration of approximately 10⁶-pfu/ml. The seeded DI was then passed through the column using the above pump at a flow rate of 5 ml/min. Fractions of the column influent and effluent were also collected after the passage of 50,100,200 ml of seeded DI. The sample were serially diluted and assayed for the respective virus and bacteria as described above. The results are indicated in Table-20.

REFERENCES

Smith, E. M. and C. P. Gerba, 1982. Laboratory methods for the growth and detection of animal viruses. In C. P. Gerba and S. M. Goyal, ed. Methods in Environmental Virology. Marcel Dekker, Inc. New York, N.Y. P. 76-88.

Berg, G., R. S. Safferman, D. R. Dahling, D. Berman, and C. J. Hurst, 1984 USEPA Manual of Methods for Virology, U.S. EPA, Cincinnati, Ohio.

Cuprous silicate immobilized on agropolymer and cupric silicate immobilized on activated alumina decontaminated Polio Lsc 1 and Rotavirus SA11 (as shown in Table 22).

Cupric silicate immobilized on agropolymer decontaminated polio Lsc1 viruses up to 55.9% when 1 gram of material was used in a column compared to 99.9% of decontamination resulted by using of 2 grams of material in a column.

Cupric silicate immobilized on agropolymer decontaminated rota viruses SA11 viruses up to 48.8% when 1 gram of material was used in a column compared to 99.9% of decontamination resulted by using of 2 grams of material in a column.

Cupric silicate immobilized on activated alumina decontaminated polio Lsc1 viruses up to 70.3% when 10 gram of material was used in a column compared to 99.3% of decontamination resulted by using of 20 grams of material in a column.

Cupric silicate immobilized on activated alumina decontaminated rota viruses SA11 up to 86.2%when 10 gram of material was used in a column compared to 99.8% of decontamination resulted by using of 20 grams of material in a column.

The cupric silicate immobilized on agropolymer and also cupric silicate activated alumina decontaminated E. coli O157:H7 bacteria.

28) Chemical Decontamination Property of Immobilized Functional Transition Metal Silicates on Silica Gel:

Functional transition metal silicates were immobilized on silica gel. Chemical contaminants such as trihalomethanes, polychlorinated biphenyls, semi volatile organic compounds, volatile organic compounds, and phenols were dissolved separately in water and passed through a column of functional transition metal silicate immobilized on silica gel (6×1 cm column at 0.5-1 ml/minute flow rate). The chemical pollutant content in treated solution was assayed by using GC-FID or GC-ECD or GC/MS/MS.

Cupric silicate immobilized on silica gel decontaminated 7.5 ppm of trihalomethanes (such as chloroform, 1,1,1, trichloroethane, tetrachloroethylene, trichloroethylene, bromodichloroethane, dibromochloroethane, tetrachloroethylene, bromoform, 1,2, dichloro-3-bromopropane) out of 8.950 ppm of trihalomethanes as shown in Table-23.

Cupric silicate immobilized on silica gel decontaminated 2.4 ppm of Polychlorinatedbiphenyls (such as 2,3-dichlorobiphenyl, trichlorobiphenyl, tetrachlorobiphenyl, pentachlorobiphenyl, hexachlorobiphenyl, heptachlorobiphenyl, octachlorobiphenyl) out of 3.5729 ppm of Polychlorinatedbiphenyls as shown in Table-27.

Cupric silicate immobilized on silica gel decontaminated 9.1 ppm of semi volatile organic compounds (such as Benzene, 1,4-dichloro; ethane hexachloro; benzene 1,2,3, trichloro; 1,3 butadiene, 1,1,2,3,4; naphthalene, 2-chloro; acenephthylene; acenapthene; phenol, 2,4-bis(1,1-imet); diethyl phthalate; fluorene; benzenel-chloro-3-phenol; diphenylamine; 4-bromophenyl-phenylether; benzene, hexachloro; phenantherene; anthracene; dibutyl phthalate; fluoranthene; pyrene; benzyl butyl phthalate; chrysene; bis(2-ethylhexy)phthalate; phenol, 2,3,4,5-tetrabrom; di-n-octyl phthalate; benzo (b) fluoranthene; benzo(k) fluoranthene; benzo(a) pyrene; indeno(1,2,3-cd)pyrene, dibenzo (a, h) anthracene; benzo(g, h, l) perylene) out of 20.8196 ppm of semi volatile organic compounds as shown in Table 24.

Cupric silicate immobilized on silica gel decontaminated 10.8 ppm, of volatile organic compounds (such as 1,1,1, trichloroethane; 1,1,2-trichloroethane; 1,3-dichloropropane; dibromochloromethane; ethane 1,2 dibromo; chlorobenzene; benzene 1,2-dimethyl; benzene 1,3-dimethyl; orthoxylene; benzene 1-methylethyl; ethane 1,1,2,2-tetrachloro; bromobenzene; 2-chloro toluene; benzene, propyl; benzene, 1 chloro 4-methyl; benzene 1,2,3-trimethyl; 4-iso propyl toluene; benzene 1,2-diethyl; benzene 1,2-dichloro; 1,3-dichlorobenzene; 1,4-dichlorobenzene; toluene; n-butylbenzene; 1,2-dibromo 3-chloropropane; 1,2,4-trichlorobenzene; naphthalene; benzene 1,2,3-trichloro; benzene 1,3,5-trichloro; benzene 1,3,4-trichloro; 1,3-butadienel,1,2,3,4; benzene 2-bromo 1,3,5; nitrobenzene; styrene; benzylbenzoate; 1,2,3,4-tetramethylbenzene; benzene 1-chloro 2-propyl; 4-bromo 3-chloroanilene) out of 18.5 ppm of volatile organic compounds as shown in Table 25.

Cupric silicate immobilized on silica gel decontaminated 2.8 ppm of phenols (such as benzoic acid; 2,4,5-trichlorophenol; 3-nitroaniline; 3-nitrophenol; 4-nitrophenol; 2,4-dinitrophenol; 4-nitroaniline; pentachlorophenol) out of 7.5234 ppm of phenols as shown in Table 26.

Zinc silicate immobilized on silica gel decontaminated 6.8 ppm of trihalomethanes (such as chloroform, 1,1,1, trichloroethane, tetrachloroethylene, trichloroethylene, bromodichloroethane, dibromochloroethane, tetrachloroethylene, bromoform, 1,2, dichlor-3-bromopropane) out of 9.1725 ppm of trihalomethanes as shown in Table 28.

Silver silicate immobilized on silica gel decontaminated 7.2 ppm of trihalomethanes (such as chloroform, 1,1,1, trichloroethane, tetrachloroethylene, trichloroethylene, bromodichloroethane, dibromochloroethane, tetrachloroethylene, bromoform, 1,2, dichlor-3-bromopropane) out of 9.1725 ppm of trihalomethanes as shown in Table 29.

Manganese silicate immobilized on silica gel decontaminated 7.5 ppm of trihalomethanes (such as chloroform, 1,1,1, trichloroethane, tetrachloroethylene, trichloroethylene, bromodichloroethane, dibromochloroethane, tetrachloroethylene, bromoform, 1,2, dichlor-3-bromopropane) out of 9.1725 ppm of trihalomethanes as shown in Table 30.

Zirconium silicate immobilized on silica gel decontaminated 5.1 ppm of trihalomethanes (such as chloroform, 1,1,1, trichloroethane, tetrachloroethylene, trichloroethylene, bromodichloroethane, dibromochloroethane, tetrachloroethylene, bromoform, 1,2, dichlor-3-bromopropane) out of 9.1725 ppm of trihalomethanes as shown in Table 31.

29) Bacterial Decontamination Property of Immobilized Functional Transition Metal Silicates Obtained by Incorporation of Functional Transition Metal Silicates into Resins (Such as Vinyl Ester, Bisphenol and Isopthalic Resins):

Bacterial coliform containing water was passed through immobilized functional transition metal silicates on column mode. The immobilized functional transition metal silicates containing resins were tested for their bacterial decontamination property. The coliform containing water (460 col/ml) was passed through 3.6 grams of immobilized functional transition metal silicates filled in a column, at a flow rate of 5 ml/min.

The decontamination was assayed by measuring bacterial colonies in a petriplate containing bacterial growth medium.

The results as shown in Table 32 indicates that immobilized functional transition metal silicates decontaminated coliform bacteria from water.

Cupric silicate immobilized on bisphenol resins (3.6 gms) decontaminated coliform up to 70% from 200 ml of (1.38×10⁵) coliform containing water.

30) Bacterial Decontamination Property of Functional Transition Metal Silicate Resin Coatings on Sand:

1 gm of cupric silicate mixed with 10 ml of isopthalic resin was coated on 100 ml volume of quartz sand (500 microns) and the coliform bacteria 3.23×10⁵/liter containing water passed through the 5×1 cm size materials in column.

Functional transition metal silicate containing resin coated quartz sand decontaminated coliform bacteria up to 28.79 and 20.12% from 500 ml and 1000 ml from 3.23×10⁵/liter coliform containing bacteria (Table 33).

31. Toxic Gases Detoxification Nature of Immobilized Functional Transition Metal Silicates:

To determine the toxic gases detoxification nature of immobilized functional transition metal silicates, the smoke emissions from combustion of kerosene engine, was passed through the immobilized functional transition metal silicates packed in 20×3 cm column.

Uniform combustion of kerosene was maintained along with controls. The toxic gases such as carbon monoxide, sulphur dioxide, and NO_(X) (oxides of nitrogen) were assayed using flew gas analyzer (testo-350) equipment. The immobilized functional transition metal silicates detoxified toxic gases from kerosene combustion (shown in Table 34).

Immobilized functional transition metal silicates also reduced the hydrocarbons released from the combustion.

32. Nicotine and Tar Detoxification Nature of Immobilized Functional Transition Metal Silicates

A mini smoking machine was fabricated to pass the cigarette smoke through immobilized functional transition metal silicate (500 mg) containing filter (a mini column packed in a 1 ml pipette plastic tip). The uniform burning of the cigarette with uniform sucking of the smoke was done by controlling suction by a vacuum pump attached to a glass chamber connected to smoking outlet of cigarette.

After passing cigarette smoke the functional transition metal silicate-containing filter was extracted with acetone.

Total content of nicotine absorbed in these filters was estimated at UV 254 nm using standard nicotine solutions (95%, standard nicotine solution, BDH, England). Total tar content was estimated by evaporating the acetone extraction of filter in a crucible. Toxic gases were estimated from the glass chamber and for comparison cigarette smoke obtained with out any filter was taken as control. As shown in Table (35) immobilized functional transition metal silicates reduced tar and nicotine significantly.

The toxic gases such as carbon monoxide, sulphur dioxide, NO_(X) (oxides of nitrogen) and hydrocarbons were assayed using flew gas analyzer (testo-350) equipment and the immobilized functional transition metal silicates containing filters detoxified toxic gases from cigarette smoke (Table 36).

This invention now will describe the salient features of functional transition metal silicates. Functional transition metal silicates having varied silicate metal ratio were synthesized and silicate or metal content enhancement or decrease in a functional transition metal silicates was done at suitable reaction conditions (at acidic or neutral or basic or extreme acidic pH conditions) and using varied reactants such as soluble silica having different alkali silica ratios.

Functional transition metal silicates synthesized at acidic pH conditions possess effective functions (decontamination of metals, chemicals, disinfection of microbes, fungicidal and bactericidal activities) than functional transition metal silicates synthesized at neutral or basic conditions.

Functional transition metal silicates synthesized at extreme acidic pH conditions by addition of acid (such as HCl or HNO₃) containing very low transition metal content also possesses functional activities such as decontamination and disinfection etc. Contrary functional transition metal silicates prepared in basic conditions with low transition metal content failed to exert effective disinfection or decontamination properties. This may be due to many reasons and one important reason is that the formation of more amount transition metal hydroxides along with silicates structure at alkaline conditions. As evidence in Tables 1 & 5, cupric silicate prepared at basic conditions even at higher doses failed to decontaminate arsenic or disinfect bacteria effectively. The transition metal silicate ratios although similar, some are functional and the others are non-functional. This variability of functionality of transition metal silicates is the topic of this invention.

Each functional transition metal silicate has its own uniqueness. Cupric silicates exhibited very strong decontamination and disinfection properties. Zinc has more freedom or capacity to interact with silica and functional zinc silicates structuring were done based on decontamination and disinfection nature. Similarly manganese silicates, silver silicates, and zirconium silicates functionality was enhanced by optimizing conditions of synthesis.

Regarding silver silicates when they were synthesized at basic or neutral pH conditions failed to absorb arsenic like toxic metals and silver silicates synthesized at extreme acidic pH conditions (by addition of nitric acid) absorbed arsenic effectively. Zirconium silicates synthesized at neutral or basic pH conditions, do not possess bacterial decontamination nature and synthesizing at acidic pH conditions zirconium silicates attained the desired bacterial decontamination property. The particle size was uniformly maintained (below 1 μm and above 0.5 μm) for testing these functional transition metal silicates.

These immobilizations in present invention can be classified as physical or chemical or incorporating directly into the resins. The selected materials for chemical immobilization (such as agropolymers, activated alumina, silica gel) has the property to bind with transition metals. Activated alumina, as it is amphoteric, passes the electron to charged copper.

Physical immobilization of functional transition metal silicates was done on cellulose, quartz sand, and by incorporating into resins. Transition metal silicate containing resins were coated on quartz sand.

The wide application of the said functional transition metal silicates is an important aspect of the invention. Accordingly the invention pertains to a method of producing immobilized transition metal silicates using activated alumina, aluminum oxide, cellulose, resins, quartz sand, and functional transition metal silicate containing resin coated quartz sand.

Now it is essential to summarize the findings of the investigations carried by the applicant in the following Tables 1 to 36.

Table 1 denotes the comparative functional and structural variability of functional transition metal silicate (cupric silicate) based on variable parameters of synthesis.

Table 2 denotes the comparative functional and structural variability of functional transition metal silicates (silver silicate, manganese silicate, zinc silicate and zirconium silicate) based on variable parameters of synthesis.

Table 3 denotes the bactericidal property of cupric silicates against Staphylococcus aureus, Bacillus subtilis, Pseudomonas aeruginosa, and E. coli.

Table 4 denotes the comparative bactericidal property of cupric silicates. Cupric silicate (silicate:transition metal ratio=1:5.15) and cupric silicate (silicate: transition metal ratio=1:1) at a concentration of 0.06 and 0.0125 were tested for comparative bactericidal property against E. coli.

Table 5 denotes the bactericidal property of zinc silicate at a concentration of 0.25% mixed in bacterial growth media, which was tested against Staphylococcus aureus.

Table 6 denotes the comparative fungicidal property of cupric silicates against Scelerotium rolfsii, Rhizoctonia solani, Fusarium oxysporium, and Pyricularia oryzae.

Table 7 denotes the viral disinfection property functional transition metal silicate (Cupric silicate).

Table 8 denotes the trihalomethanes decontamination property of cupric silicate.

Table 9 denotes the arsenic decontamination of immobilized functional transition metal silicates on activated alumina (size: above 1000 microns).

Table 10 denotes the arsenic decontamination of immobilized functional transition metal silicates on different sizes on activated alumina.

Table 11 denotes the arsenic decontamination of immobilized functional transition metal silicates on agropolymers.

Table 12 denotes the decontamination property of transition metal substances by physical immobilization on quartz sand (250-500 microns size).

Table 13 denotes the mercury decontamination property of immobilized functional transition metal silicates on activated alumina and agropolymer.

Table 14 denotes the protein decontamination property of functional transition metal silicate immobilized on agropolymers.

Table 15 denotes the pesticidal decontamination nature of functional transition metal silicate immobilized on agropolymers.

Table 16 denotes the bacterial (coliform) decontamination of immobilized functional transition metal silicates on activated alumina.

Table 17 denotes the bacterial decontamination of immobilized functional transition metal silicates on agropolymers.

Table 18 denotes the bacterial decontamination property of immobilized functional transition metal silicates on aluminium oxides, and cellulose.

Table 19 denotes the bacterial decontamination property of immobilized functional transition metal silicates on quartz sand.

Table 20 denotes the decontamination of fungus (Aspergillus species) from a long time (6 months) stored water by using immobilized functional transition metal silicates.

Table 21 denotes the protozoan (Cryptosporidium parvum) decontamination property of immobilized functional transition metal silicates on agropolymer.

Table 22 denotes the viral decontamination property of immobilized functional transition metal silicates and E. coli decontamination nature of immobilized functional transition metal silicates.

Table 23 denotes the trihalomethanes decontamination property of cupric silicate immobilized on silica gel.

Table 24 denotes the semi volatile organic compounds decontamination property of cupric silicate immobilized on silica gel.

Table 25 denotes the volatile organic compounds decontamination property of cupric silicate immobilized on silica gel.

Table 26 denotes the phenols decontamination property of cupric silicate immobilized on silica gel.

Table 27 denotes the polychlorinated biphenyls decontamination property of cupric silicate immobilized on silica gel.

Table 28 denotes the trihalomethanes decontamination property of zinc silicate immobilized on silica gel.

Table 29 denotes the trihalomethanes decontamination property of silver silicate immobilized on silica gel.

Table 30 denotes the trihalomethanes decontamination property of manganese silicate immobilized on silica gel.

Table 31 denotes the trihalomethanes decontamination property of zirconium silicate immobilized on silica gel.

Table 32 denotes the bacterial decontamination property of immobilized functional transition metal silicates (5%) incorporated in to resins.

Table 33 denotes the bacterial decontamination property of functional transition metal silicate resin coatings on sand.

Table 34 denotes the toxic gas (engine combustion) detoxification (%) nature of immobilized functional transition metal silicates.

Table 35 denotes the tar and nicotine absorption property of immobilized functional transition metal silicates.

Table 36 denotes the cigarette smoke detoxification nature (%) of immobilized functional transition metal silicates.

The results derived from the present invention gives a scope of synthesizing functional transition metal silicates (such as cupric silicate, silver silicate, manganese silicate, zinc silicate) and functional transition metal silicates immobilized on materials such as activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, resins (vinyl ester, bisphenol and isopthalic food grain resins), and functional transition metal silicates incorporated resins and functional transition metal silicate containing resin coated sand having varied metal silicate ratio exhibiting varied functions which are useful in various other applications such as manufacturing of catalysts, and hybridizing or doping with zeolites. TABLE 1 COMPARISION OF FUNCTIONAL TRANSITION METAL SILICATES Name of Silica:transition ESR S. No the material Parameters of synthesis metal ratio G values 1 Cupric Acidic conditions with 10 ml of sodium 1:5.15 A) 4.32481 silicate silicate [1:2] + 100 ml of 0.5 gm/ml transition B) 2.66205 metal salt solution C) 2.31749 D) 2.08807 E) 2.04673 2 Cupric Acidic conditions at 70° C. to 90° C. with 50 ml 1:0.78 A) 2.23480 silicate sodium silicate [1:1] + 100 ml of 0.5 gm/ml B) 2.06456. transition metal salt solution 3 Cupric Neutral conditions with sodium silicate 1:1 A) 3.10383 silicate [1:1] + 100 ml of 0.5 gm/ml transition metal B) 2.36522 salt solution C) 2.0467 D) 1.21887 E) 0.96686 4 Cupric Basic conditions with sodium silicate 1:0.8 A) 3.71806 silicate [1:1] + 100 ml 0.5 gm/ml transition metal B) 3.23001 salt solution C) 2.61681. 5 Cupric Extreme Acidic conditons at 70° C. to 90° C. 1:0.63 A) 2.18421 silicate with addition of 10 ml of 36% HCl and B) 2.06874 sodium silicate [1:1] + 100 ml of 0.5 gm/ml C) 1.21231. transition metal salt solution. 6 Cupric Extreme Acidic conditions at 60° C. to 70° C. 1:0.34 A) 2.15561 silicate with addition of 20 ml 36% HCl and B) 2.03614 sodium silicate [1:1] + 100 ml of 0.5 gm/ml transition metal salt solution. Weight of the Weight of material the XRD for % Bacterial material % Peak height, bacterial decontamination for arsenic Arsenic (counts/s) and decontamination from decontamination decontamination S. No Angle(° 2 theta) (mg/Lt) 2.72 × 10⁵ (mg/100 ml) from 2.5 ppm 1 1) 2128.25 and 10 99 50 69 18.28197 2) 1583.74 and 32.29018 3) 1470.73 and 39.79307 2 1) 835.63 and 10 99 50 55.8 16.20057 2) 706.74 and 32.23910 3) 602.62 and 39.57159 3 1) 940.91 and 10 99 50 277 16.19577 2) 764.43 and 32.29278 3) 694.85 and 39.77809 4 1) 152.74 and 250 21.69 60 6 26.64983 5 1) 400.70 and 10 99 50 42 16.19872 2) 394.77 and 32.27956 3) 330.02 and 39.71761 6 1) 541.23 and 10 99 50 27.7 16.28305 2) 414.21 and 32.36589 3) 365.45 and 39.85131

TABLE 2 COMPARISION OF FUNCTIONAL TRANSITION METAL SILICATES Silica:transition Name of the metal ESR S. No material Parameters of synthesis ratio G values  7 Zinc silicate Neutral conditions with sodium silicate [1:1] + 100 ml 1:12.13 A) 5.49809 of 0.5 gm/ml transition metal salt solution B) 4.55342 C) 2.54593 D) 2.10091 E) 2.05499  8 Zinc silicate Extreme acidic conditions at 70° C. to 90° C. with 1:2.46 A) 4.38410 addition of 10 ml of 38% HCl and sodium silicate B) 4.01910 [1:1] + 100 ml of 0.5 gm/ml transition metal salt C) 2.53191 solution. D) 1.87888 E) 2.01793  9 Silver silicate Neutral conditions with sodium silicate [1:2] + 100 ml 1:19.57 A) 4.36796 of 0.5 gm/ml transition metal salt solution. B) 2.37847 C) 3.95509 D) 2.04657 10 Silver silicate Extreme acidic reaction at 70° C. to 90° C. 1:1.04 A) 4.37171 conditions with addition of 8 ml of 69-70% HNO₃ B) 4.04714 and sodium silicate [1:1] + 100 ml of 0.5 gm/ml C) 1.98189 metal salt solution 11 Manganese Neutral conditions with sodium silicate 1:1.94 A) 1.93412 silicate [1:1] + 100 ml of 0.5 gm/ml transition metal salt B) 2.08855 solution. 12 Manganese Extreme acidic conditions at 70° C. to 90° C. with 1:1.09 A) 4.34836 silicate addition of 10 ml of 38% HCl and sodium B) 4.17458 silicate[1:1] + 100 ml of 0.5 gm/ml transition C) 2.18228 metal salt solution. D) 2.11243 E) 2.05491 F) 1.999661 13 Zirconium Neutral conditions with sodium silicate [1:1] + 100 ml 1:2.90 A) 4.42797 silicate of 0.5 gm/ml transition metal salt solution B) 4.18272 C) 2.24547 D) 2.30425 E) 2.1896 F) 1.23088 14 Zirconium Extreme acidic conditions at 70° C. to 90° C. with 1:0.77 A) 4.37236 silicate addition of 10 ml of 35% HCl and sodium B) 2.82039 silicate [1:1] + 100 ml of 0.5 gm/ml transition C) 1.92596 metal salt solution. D) 1.21852 E) 1.02930 F) 0.93795 Weight of Weight of the XRD the material % Bacterial material for % Peak height, for bacterial decontamination arsenic Arsenic (counts/s) and decontamination from decontamination decontamination S. No Angle(° 2 theta) (mg/Lt) 2.72 × 10⁵ (mg/100 ml) from 2.5 ppm  7 1) 444.15 and 250 96.58 100 98.7 32.75904 2) 307.02 and 59.58455 3) 283.38 and 28.27638  8 1) 2078.88 and 250 99.76 100 72.3 11.07467 2) 835.44 and 33.52527 3) 664.98 and 32.88120  9 1) 3945.11 and 5 99.5 100 4.5 32.29885 2) 2421.27 and 48.27448 3) 1835.68 and 27.89129 10 1) 2217.87 and 5 99.5 100 99 29.33483 2) 684.55 and 47.68093 3) 674.27 and 42.31091 11 1) 148.04 and 500 51.68 100 12.4 30.65087 12 1) 32.88 and 500 58.8 100 10.3 24.65599 13 — 250 2.0 100 28.9 14 1) 84.80 and 250 98.8 100 54.5 10.89433

TABLE 3 Bactericidal property of cupric silicates: Material embedded Material Silica:transition- in LB concen- metal agar media tration ratio Test bacteria Result Cupric 0.25% 1:5.15 Staphylococus No growth silicate aureus was observed Cupric 0.25% 1:5.15 Pseudomonas No growth silicate aeruginosa was observed Cupric 0.25% 1:5.15 Bacillussubtilis No growth silicate was observed Cupric 0.25% 1:5.15 Eschericia No growth silicate coli was observed Control Significant growth was observed

TABLE 4 Comparative bactericidal property of cupric silicates: Name Name of Silica:transition of the Material Concentration the sample metal ratio pathogen 0.06% 0.125% Cupric silicate 1:5.15 Eschericia Significant No growth Synthesized coli growth was at acidic was observed reaction observed conditions Cupric silicate 1:1   Eschericia Significant Significant synthesized at coli growth was growth was neutral reaction observed observed conditions Control Eschericia Significant growth was Coli Observed

TABLE 5 Bactericidal property of Zinc silicate Material embedded Material in LB concen- Silica:transition Test agar media tration metal ratio Bacteria Results Zinc silicate 0.25% 1:12 Staphylococus No growth aureus was observed Control Significant growth was observed

TABLE 6 Comparative fungicidal property of cupric silicates: Percent reduction in colony Name of the Silica:transition diameter over control sample metal ratios Name of the pathogen 0.0625% 0.125% 0.25% Cupric 1:5.15 a) Sclerotium rolfsii. 0 0 32.93 silicate b) Rhizoctonia solani 47.7 61.9 73.2 synthesized c) Fusarium oxysporium 57.8 70.0 76.8 at acidic pH d) Pyricularia oryzae 74.2 86.2 100 reaction conditions Cupric 1:0.78 a) Sclerotium rolfsii. 0.0 0.0 24.7 silicate b) Rhizoctonia solani 22.9 44.0 59.0 synthesized c) Fusarium 0.0 0.0 68.3 at neutral pH oxysporium reaction d) Pyricularia oryzae 72.7 85.5 88.5 conditions

TABLE 7 Viral disinfection property of functional transition metal silicate (cupric silicate) Percentage reduction (%) of bacteriophages Name of the Material MS-2 ØX174 PRD-1 Cupric Batch a 91 88 96 silicate Batch b 89 95 94 Batch c 94 92 98

TABLE 8 Trihalomethanes decontamination property of cupric silicate Concentra- tion of Decon- (control) tamination contaminant ability of the Name of the solution Retained absorbant S. No. compound (ppm) (ppm) (ppm) 1 Chloroform 0.9975 0.4146 5.4 ppm of 2 1,1,1 Trichloroethane 1.0016 0.4476 THM mix 3 Tetrachloroethylene 1.0005 0.6573 4 Trichloroethylene 1.0006 0.4064 5 Bromodichloroethane 1.0008 0.8012 6 Dibromochloroethane 1.0003 0.7861 7 Tetrachloroethylene 0.9987 0.6795 8 Bromoform 0.9907 0.5455 9 1,2,Dichloro- 0.9423 0.6557 3-Bromopropane Total Concentration of 8.950 5.3939 THM mix

TABLE 9 Arsenic decontamination of immobilized functional transition metal silicates on activated alumina (size: above 1000 microns) Percentage of arsenic decontamination after treatment of 2.12 ppm arsenic containing water by passing through S. No Name of the material 10 cms size column at flow rate 10 ml/min 1 Cupric Silicate 90.10 2 Zinc Silicate 91.98 3 Manganese Silicate 58.96 4 Zirconium Silicate 13.68

TABLE 10 Arsenic decontamination property of immobilized transition metal silicate (cupric silicate) on different sizes of activated alumina Amount of arsenic content in ppm after treatment of 1 liter sodium arsenate (2.4 ppm solution) in a % 10 cm column at 10 ml/min decontam- S. No Name of the material flow rate ination 1 Cupric silicate (500 nm) 0.114 95.58 2 Cupric silicate (1000 nm) 0.36 86.05 3 Control (1000 nm) 0.68 73.64 (activated alumina) 4 Control solution 2.4 0 (without treatment)

TABLE 11 Arsenic decontamination property of transition metal silicate (cupric silicate) immobilized on agropolymers % decontamination of arsenic from 500 ppb of arsenic S. No. Name of the material treated solution 1 Cupric silicate immobilized on 56.48 agropolymer (250 mg)

TABLE 12 Decontamination property of functional transition metal silicates by physical immobilization on quartz sand (250-500 microns size) Percentage of arsenic decontamination after treatment of 2.12 ppm arsenic containing water by passing through 10 cm size of the S. No Name of the material column at flow rate 10 ml/min. 1 Cupric silicate 35 2 Zinc silicate 48.58 3 Manganese silicate 18.87 4 Zirconium silicate 8.49 5 Sand as control 1.88

TABLE 13 Mercury decontamination property of immobilized functional transition metal silicates on activated alumina and agropolymer Mercury content (ppb) Initial after 60 min of Mercury treatment with content (ppb) immobilized functional S. in a liter transition metal No. Name of material water silicates (1 mg/ml). 1 Cupric silicate immobilized 224.21 Below detectable on agropolymer limits 2 Cupric silicate immobilized 224.21 Below detectable on activated alumina limits 3 Control 224.21 224.21

TABLE 14 Protein decontamination property of functional transition metal silicates immobilized on agropolymers Protein binding (mg) after treatment with 100 ml of BSA solution (1 mg/ml concentration), 2 cm column at S. No Name of the material 8 ml/min flow rate. 1 Silver silicate 10.0 2 Cupric silicate 15.4 3 Zinc silicate 3.0

TABLE 15 Pesticidal decontamination nature of functional transition metal silicate immobilized on agropolymers % decontamination from 10 ppm pesticide Name of solution by 1 gm of sample in a column S. No the material Endosulphan Cypermethrin Chlorpyriphos 1 Cupric silicate 59.7 62.4 46.6 immobilized on activated alumina 2 Cupric silicate 61.7 83.4 49.1 immobilized on agropolymer

TABLE 16 Bacterial (coliform) decontamination property of immobilized functional transition metal silicates on activated alumina Percentage of coliform decontamination after treating 500 ml of coliform (5 × 10⁵) containing water at a flow rate of 10 ml/min from 10 cms length column of functional transition metal silicates S. No. Name of the material immobilized on activated alumina 1. Silver silicate 98 2. Zinc silicate 43 3. Cupric silicate 83 4. Alumina as control Below 0.1

TABLE 17 Bacterial decontamination property of immobilized transition metal silicates on agropolymers Volume (ml) of the coliform bacteria 4 × 10⁴/liter containing water passed through the column containing 250 mg of immobilized transition metal % S. No Type of material silicate on agropolymer decontamination 1 Cupric silicate 2000 99 immobilized on 2500 97.45 Agropolymer 3000 94.87 2 Silver silicate 3000 99 immobilized on Agropolymer 3 Zinc silicate 1000 61.90 immobilized on 1500 14.28 Agropolymer 2000 4.76

TABLE 18 Bacterial decontamination property of immobilized transition metal silicates on aluminium oxide and cellulose. Volume(ml) of Weight coliform of containing water Type of material material (460 col/ml) selected for in the passed through % S. No immobilization column column decontamination 1 Aluminium oxide  1.0 gm 250 93.47 (Al₂O₃) 2 Cellulose 0.97 gm 300 93.71 3 Control 460 coliform col/ml 100 (untreated water)

TABLE 19 Bacterial decontamination property of immobilized transition metal silicates on quartz sand Percentage of coliform decontamination after Bacterial coliform treating 500 ml coliform amount (per 500 ml) containing water at a present before flow rate of 10 ml/min Name of the treating with from 10 cms length material functional transition column of functional immobilized on metal silicates in transition metal silicates S. No quartz sand column coated on quartz sand 1 Cupric silicate 3.88 × 10⁵ 83 2 Zinc silicate 3.62 × 10⁵ 34 3 Manganese 3.78 × 10⁵  5 silicate 4 Zirconium silicate 2.90 × 10⁵  6 5 Sand as control  1.1 × 10⁶ Below 0.001

TABLE 20 Decontamination property of fungus (Aspergillus species) from a long time (6 months) stored water by using immobilized cupric silicate on agropolymer. Volume of water (ml) passed Type of Column through S. No. material size column Result 1 Cupric silicate 2 cm 1 liter No growth of fungus immobilized on was observed when Agropolymers the treated water was placed on fungal growth media 2 Control Growth of fungus was observed when the untreated water was placed on fungal growth media

TABLE 21 Protozoan (Cryptosporidium parvum) decontamination property of immobilized functional transition metal silicates on agropolymer Volume of the % Reduction of seeded Name of the fraction passed Cryptosporidium parvum sample through column oocysts Cupric Fraction-A (20 ml) >99.99 Silicate Fraction-B (50 ml) >99.99 immobilized Fraction-C (80 ml) >99.99 on agropolymer

TABLE 22 A. Viral decontamination property of immobilized functional transition metal silicates B. E. Coli decontamination nature of immobilized functional transition metal silicates Percent reduction (%) Weight of the A B sample used in Rotavirus E. coli Sample column Polio Lsc 1 SA11 O157:H7 Cupric silicate  1 gram 55.9 48.8 99.4 immobilized on  2 grams 99.998 99.991 99.99 agropolymer Cupric silicate 10 grams 70.3 86.2 91.9 immobilized on 20 grams 99.3 99.8 99.5 activated alumina

TABLE 23 Trihalomethanes decontamination property of cupric silicate immobilized on silica gel Decon- Concentration tamination of control ability contaminant of the S. Name of solution Retained absorbent No. the compound (ppm) (ppm) (ppm) 1 Chloroform 0.9975 0.9501 7.5 ppm of 2 1,1,1 Trichloroethane 1.0016 0.9689 THM mix 3 Tetrachloroethylene 1.0005 0.9362 4 Trichloroethylene 1.0006 0.9650 5 Bromodichloroethane 1.0008 0.8897 6 Dibromochloroethane 1.0003 0.7885 7 Tetrachloroethylene 0.9987 0.9041 8 Bromoform 0.9907 0.7308 9 1,2Dichloro-3- 0.9423 0.4059 Bromopropane Total Concentration 8.950 7.5392 of THM mix

Chromatographic Conditions for estimation of Trihalomethanes GC: VARIAN CP 3800 with Head Space Column: ZB-5 30 m × 0.25 u × 0.25 Oven temperature: 35° C./5 min @ 10° C./min 250° C./1 min Detector: Electron Capture Detector Detector Temperature: 300° C. Injection Temperature: 200° C. with split less mode Carrier gas: Nitrogen Flow: 0.5 ml/min Makeup gas flow: 29 ml/min Range: 1.0 Run time: 27.473 min

TABLE 24 Semi volatile organic compounds decontamination property of cupric silicate (immobilized on silica gel) Concentration of Decontamination control ability of contaminant the absorbent S. No. Name of compound solution (ppm) Retained (ppm) (ppm) 1 Benzene, 1,4,-dichloro 0.696 0.17 9.1 ppm of the 2 Ethane Hexachloro 0.860 0.546 SVOCs mix. 3 Benzene 1,2,3, trichloro 0.8806 0.184 4 1,3 Butadiene, 1,1,2,3,4 0.775 0.437 5 Naphthalene, 2-chloro 0.876 0.644 6 Acenaphthylene 0.812 0.526 7 Acenapthene 0.775 0.488 8 Phenol, 2,4-bis(1,1-imet 0.351 0.000 9 Diethyl Phthalate 0.768 0.467 10 Fluorene 0.793 0.518 11 Benzene 1-chloro-3pheno 0.574 0.386 12 Diphenylamine 0.634 0.568 13 4-Bromophenyl- 0.861 0.632 phenylether 14 Bezene, hexachloro 0.542 0.310 15 Phenantherene 0.772 0.465 16 Anthracene 0.812 0.528 17 Dibutyl phthalate 0.693 0.275 18 Fluoranthene 0.706 0.276 19 Pyrene 0.700 0.252 20 Benzyl butyl phthalate 0.691 0.187 21 Chrysene 0.644 0.206 22 Bis(2- 0.676 0.134 ethylhexyl)phthalate 23 Phenol, 2,3,4,5-tetrabrom 0.671 0.124 24 Di-n-octyl phthalate 0.729 0.105 25 Benzo(b) Fluoranthene 0.698 0.061 26 Benzo(k) fluoranthene 0.670 0.066 27 Benzo (a) pyrene 0.680 0.035 28 Indeno(1,2,3-cd) pyrene 0.533 0.000 29 Dibenzo(a,h) anthracene 0.430 0.43 30 Benzo(g,h,l) perylene 0.517 0.039 Total Concentration of 20.8196 9.059 SVOCS Mix

Chromatographic conditions for estimation of semi volatile organic compounds GC MS: VARIAN CP 3800 WITH GC-MS SATURN 2000 GC/MS/MS. Column: WCOT Fused silica 30 M × 0.25 mm Id, Coating CP-SIL 8 CB Low Bleed/MS DF: 0.25. Cat. No: CP 5860 Oven temperature: 60° C. @ 7.0° C./min, 130° C. @ 5.0° C./ min, 200° C. @ 6.0° C./min, 260° C. @ 20.0° C./min, 280° C. @ 15 min. Injection Temperature: 280° C. with split less mode. Carrier Gas: Helium Flow Rate: 1.0 ml/min. Run time: 50.0 min. MS Conditions: Emission Current: 10 micro amps. Mass Defect: 0 mmu/100 u Count Threshold: 2 counts. Multiplier offset: 0 volts Cal Gas: OFF Scan Time: 0.810 seconds Segment start time: 3.00 minutes. Segment end time: 50.00 minutes. Segment low mass: 45 m/z Segment high Mass: 450 m/z Ionization Mode: EI AGC Ion preparation Technique: NONE

TABLE 25 Volatile organic compounds decontamination property of cupric silicate (immobilized on silica gel) Concentration Decontamination of control of the contaminant absorbent S. No. Name of compound solution (ppm) Retained (ppm) (ppm) 1 1,1,1-Trichloroethane 0.500 0.500 10.8 ppm of 2 1,1,2-Trichloroethane 0.500 0.500 VOC mix 3 1,3-Dichloropropane 0.500 0.500 4 Dibromochloromethane 0.500 0.500 5 Ethane 1,2-Dibromo 0.500 0.500 6 Chlorobenzene 0.500 0.469 7 Benzene 1,3-dimethyl 0.500 0.500 8 Orthoxylene 0.500 0.500 9 Benzene 1-methylethyl 0.500 0.500 10 Ethane 1,1,2,2-Tetrachloro 0.500 0.488 11 Bromobenzene 0.500 0.347 12 2-chloro Toluene 0.500 0.182 13 Benzene, propyl 0.500 0.168 14 Benzene, 1Chloro 4- 0.500 0.246 methyl 15 Benzene 1,2,3-Trimethyl 0.500 0.229 16 4-Iso propyl Toluene 0.500 0.281 17 Benzene 1,2-Diethyl 0.500 0.281 18 Benzene 1,2-Dichloro 0.500 0.328 19 1,3-Dichlorobenzene 0.500 0.346 20 1,4-Dichlorobenzene 0.500 0.477 21 Benzene 1,3,4-trichloro 0.500 0.500 22 1,3-Butadiene1,1,2,3,4 0.500 0.007 23 Benzene 2-Bromo 1,3,5 0.500 0.281 24 Nitrobenzene 0.500 0.500 25 Styrene 0.500 0.051 26 Benzylbenzoate 0.500 0.100 27 1,2,3,4- 0.500 0.122 Tetramethylbenzene 28 Benzene 1-Chloro 2- 0.500 0.325 propyl 29 4-Bromo 3-chloroanilene 0.500 0.097 Total Concentration of 18.500 10.825 VOCs mix

Chromatographic conditions for estimation of volatile organic compounds GC MS: VARIAN CP 3800 WITH GC-MS SATURN 2000 GC/MS/MS. Column: WCOT Fused silica 30 M × 0.25 mm Id, Coating CP-SIL 8 CB Low Bleed/MS DF: 0.25 Cat. No: CP 5860 Oven temperature: 40° C./10 min @ 3.0° C./min, 200° C./ 10 min. Injection Temperature: 200° C. with split less mode. Carrier Gas: Helium Flow Rate: 1.0 ml/min. Run time: 50.0 min. MS Conditions: Emission Current: 10 micro amps. Mass Defect: 0 mmu/100 u Count Threshold: 2 counts. Multiplier offset: 0 volts Cal Gas: OFF Scan Time: 0.810 seconds Segment start time: 3.00 minutes. Segment end time: 50.00 minutes. Segment low mass: 45 m/z Segment high Mass: 450 m/z Ionization Mode: EI AGC Ion preparation Technique: NONE

TABLE 26 Phenols decontamination property of cupric silicate (immobilized on silica gel) Concentration of Decontamination control Re- ability of S. contaminant tained the absorbant No. Name of compound solution (ppm) (ppm) (ppm) 1 Benzoic Acid 1.086 0.3475 2.8 ppm of 2 2,4,5- 0.7083 0.1077 Phenols mix Trichlorophenol 3 3-Nitroaniline 1.3042 0.3402 4 4-Nitrophenol 1.1396 0.5004 5 2,4-Dinitrophenol 1.0523 0.5258 6 4-Nitroaniline 1.0898 0.5351 7 Pentachlorophenol 1.1432 0.4607 Total Concentration 7.5234 2.8175 of Phenols mix

Chromatographic Conditions for estimation of Phenols GC: VARIAN CP 3800 with Head Space Column: ZB-WAX 30 m × 0.25 u × 0.25 Oven temperature: 110° C./2 min @ 10° C./min 250° C./1 min Detector: Flame Ionization Detector Detector Temperature: 275° C. Injection Temperature: 250° C. with split less mode Carrier gas: Nitrogen Flow: 1.0 ml/min Range: 12

TABLE 27 Polychlorinated biphenyls decontamination property of cupric silicate immobilized on silica gel Concentration Decontamination of control ability of contaminant the absorbant S. No. Name of compound solution (ppm) Retained (ppm) (ppm) 1 2,3-Dichlorobiphenyl 0.4677 0.2723 2.4 ppm of 2 Trichlorobiphenyl 0.5312 0.2958 PCB mix 3 Tetrachlorobiphenyl 0.5279 0.3426 4 Pentachlorobiphenyl 0.5174 0.3501 5 Hexachlorobiphenyl 0.5094 0.3687 6 Heptachlorobiphenyl 0.5015 0.4161 7 Octachlorobiphenyl 0.5178 0.3845 Total Concentration of PCB 3.5729 2.43 mix

Chromatographic Conditions for estimation of Polychlorinated Biphenyls. GC: VARIAN CP 3800 with Head Space Column: ZB-5 30 m × 0.25 u × 0.25 Oven temperature: 110° C./1 min @20° C./min 280° C./10 min Detector: Electron Capture Detector Detector Temperature: 300° C. Injection Temperature: 250° C. with Split less mode Carrier gas: Nitrogen Flow: 1.0 ml/min Makeup gas Flow: 29 ml/min Range: 1.0 Run Time: 19.50 min

TABLE 28 Trihalomethanes decontamination property of zinc silicate immobilized on silica gel Concentration of Decontamination control ability of Name of the contaminant the absorbant S. No. compound solution (ppm) Retained (ppm) (ppm) 1 Chloroform 1.0380 0.2471 6.8 ppm of 2 1,1,1 Trichloroethane 0.9857 0.9857 THM mix 3 Tetrachloroethylene 1.0083 0.6021 4 Trichloroethylene 1.0110 0.7881 5 Bromodichloroethane 1.0243 0.9311 6 Dibromochloroethane 1.0302 0.8841 7 Tetrachloroethylene 1.0117 0.7733 8 Bromoform 1.0314 0.7056 9 1,2 Dichloro-3- 1.0319 0.8541 Bromopropane Total Concentration of 9.1725 6.7712 THM mix

TABLE 29 Trihalomethanes decontamination property of silver silicate immobilized on silica gel Concentration of control Decontamination contaminant ability of the S. No. Name of compound solution (ppm) Retained (ppm) absorbant (ppm) 1 Chloroform 1.038 0.5317 7.2 ppm of THM 2 1,1,1 Trichloroethane 0.9857 0.9857 mix 3 Tetrachloroethylene 1.0083 0.6784 4 Trichloroethylene 1.011 0.7789 5 Bromodichloroethane 1.0243 0.8685 6 Dibromochloroethane 1.0302 0.8543 7 Tetrachloroethylene 1.0117 0.8872 8 Bromoform 1.0314 0.8542 9 1,2 Dichloro-3- 1.0319 0.7367 Bromopropane Total Concentration of 9.1725 7.1756 THM mix

TABLE 30 Trihalomethanes decontamination property of manganese silicate immobilized on silica gel Decon- Concentration tamination of control ability of S. Name of contaminant Retained the absorbant No. the compound solution (ppm) (ppm) (ppm) 1 Chloroform 1.038 0.6732 7.5 ppm of 2 1,1,1 Trichloroethane 0.9857 0.9857 THM mix 3 Tetrachloroethylene 1.0083 0.0000 4 Trichloroethylene 1.011 0.9011 5 Bromodichloroethane 1.0243 0.9928 6 Dibromochloroethane 1.0302 0.9975 7 Tetrachloroethylene 1.0117 0.9916 8 Bromoform 1.0314 0.9921 9 1,2Dichloro-3- 1.0319 0.9604 Bromopropane Total Concentration of 9.1725 7.4944 THM mix

TABLE 31 Trihalomethanes decontamination property of zirconium silicate immobilized on silica gel Decon- Concentration tamination of control ability of the S. Name of the contaminant Retained absorbant No. compound solution (ppm) (ppm) (ppm) 1 Chloroform 1.038 0.2227 5.1 ppm of 2 1,1,1 Trichloroethane 0.9857 0.7011 THM mix 3 Tetrachloroethylene 1.0083 0.4120 4 Trichloroethylene 1.011 0.6268 5 Bromodichloroethane 1.0243 0.7130 6 Dibromochloroethane 1.0302 0.6321 7 Tetrachloroethylene 1.0117 0.8006 8 Bromoform 1.0314 0.4384 9 1,2 Dichloro-3- 1.0319 0.5112 Bromopropane Total Concentration 9.1725 5.0579 of THM mix

TABLE 32 Bacterial decontamination property of immobilized functional transition metal silicates (5%) incorporated in to bisphenol resins Volume (ml) Type of material Weight of coliform selected for of containing water % incorporation material (4.6 × 10⁵/liter) passed decontamination Cupric silicate (5%) 3.6 gm 200 70 incorporated into Bisphenol resins

TABLE 33 Bacterial decontamination property of functional transition metal silicate resin coatings on quartz sand Volume (ml) of the coliform bacteria 3.23 × 10⁵/liter containing water passed S. through the 5 cm size % No Type of material materials in column decontamination 1 1 gm of cupric silicate 500 28.79 mixed with 10 ml of 1000 20.12 isopthalic resin was coated on 100 ml volume of quartz sand (500 microns)

TABLE 34 Toxic gas (engine combustion) detoxification (%) nature of immobilized functional transition metal silicates S. Column No_(x) (oxides of No Material size nitrogen) % So₂ % 1 Cupric silicate immobilized on 20 cm 46.8 88.1 silica gel 2 Zinc silicate immobilized on 20 cm 16.57 93.76 silica gel 3 Silver silicate immobilized on 20 cm 36.0 92.5 silica gel 4 Manganese silicate 20 cm 22.45 91.13 immobilized on silica gel 5 Cupric silicate containing resin 20 cm 43.67 96.05 coated on quartz sand 6 Silica as control 20 cm 17.2 94.0

TABLE 35 Tar and nicotine absorption property of immobilized functional transition metal silicates Tar amount (mg) Nicotine amount absorbed by (mg) absorbed Immobilized by immobilized S. functional transition functional transition No Name of the sample metal silicate metal silicate 1 Zinc silicate on Silica gel 17.0 0.60 2 Manganese silicate on 22.75 0.59 silica gel 3 Cupric silicate on silica 26.25 0.73 gel 4 Silver silicate on silica 14.5 0.30 gel 5 Zirconium silicate on 2.5 0.29 Alumina Brand name of Cigarette: Charms (normal) Cigarette length: 6 cm, average weight: 0.775 grams.

TABLE 36 Cigarette smoke detoxification nature (%) of immobilized functional transition metal silicates Name of Weight the Immobilized of the CO % No_(x) % SO₂ % Hydrocarbons % S. No. materials on materials detoxification detoxification detoxification detoxification 1 Cupric Silica gel 500 mg 68.2 64.86 63.96 44.85 silicate 2 Manganese Silica gel 500 mg 54.2 32.43 40.5 29.0 silicate 3 Zinc Silica gel 500 mg 38.5 23.4 12.6 34.2 Silicate 4 Zirconium Alumina 500 mg 73.34 68.46 71.17 44.11 silicate 5 Cupric Agropolymer 300 mg 66.29 63.96 67.56 34.55 silicate Cigarette weight: 0.775 grams. Brand name of Cigarette: Charminar (normal) Cigarette length: 6 cm, average weight: 0.775 grams. 

1. Functional transitional metal silicates (FTMS) having transitional metal to silica ratio in the range of 0.34 to 19.57, variable functions resulting from different metal silicate ratios and also having variable functional structure for same transitional metal to silica ratio, exhibiting properties selected from the group comprising of decontaminant, disinfectant, protectant, microbicide or combination thereof and prepared by the process comprising the steps of a. adding a transitional metal salt solution to a soluble alkali silicate solution to form a mixture; b. forming a precipitate of a transitional metal silicate, and c. washing and drying the precipitate thus formed to obtain the transitional metal silicate characterized in that in step (a), the ratio between the transitional metal salt solution to the alkali silicate solution is varied, the temperature at which the solutions are mixed is varied between 20 to 90 C, and the pH of the medium is varied between extremely acidic condition to extremely basic condition, preparing variable functional structure for same transitional metal to silica ratio at varied conditions, also having variable functional structure for same transitional metal to silica ratio, and said FTMS capable of being immobilized on a suitable material or incorporating into resins and/or coating along with resins on suitable materials.
 2. Functional transitional metal silicates (FTMS) having transitional metal to silica ratio in the range of 0.34 to 19.57, variable functions resulting from different metal silicate ratios and also having variable functional structure for same transitional metal to silica ratio, exhibiting properties selected from the group comprising of decontaminant, disinfectant, protectant, microbicide or combination thereof and prepared by the process comprising the steps of: a. adding a transitional metal salt solution to a soluble alkali silicate solution to form a mixture; b. forming a precipitate of a transitional metal silicate, and c. washing and drying the precipitate thus formed to obtain the transitional metal silicate characterized in that in step (a), the ratio between the transitional metal salt solution to the alkali silicate solution is varied, the temperature at which the solutions are mixed is varied between 20° to 90° C., and the pH of the medium is varied between extremely acidic condition to extremely basic condition.
 3. Functional transitional metal silicate as claimed in claim 1, wherein the same are selected from the group consisting of cupric silicate, silver silicate, zinc silicate, manganese silicate, zirconium silicate and combinations thereof.
 4. Functional transitional metal silicate as claimed in claim 1, wherein the transitional metal salt solution is a transitional metal chloride solution or a transitional metal sulphate solution or a transitional metal nitrate solution or any other transitional metal salt solution such as acetate.
 5. Functional transitional metal silicate as claimed in claim 1, wherein the alkali silicate solution is sodium silicate or potassium silicate solution or any other alkali silicate solution such as calcium silicate.
 6. Functional transitional metal silicate as claimed in claim 3, wherein the cupric silicate has silicate to copper ratio in the range of 1:0.78 to 1:5.15.
 7. Functional transitional metal silicate as claimed in claim 6, wherein cupric silicate having silicate to copper ratio of about 1:
 5. 15 possessed the following properties when prepared under acidic conditions: characteristic g values of the peaks as obtained by the electron spin resonance spectrometer being (a)
 4. 3; (b) 2.5; (c)
 2. 3; (d) 2.0 and (e) 2.0; X-ray diffraction analysis having 3 significant peaks at 16.2,
 32. 2 and 39.7 having peak heights of 2128, 1593 and 1470 respectively; exhibiting decontamination property of metals such as arsenic, bacterial disinfecting property, anti-bacterial property, antifungal property, viruses disinfecting property and chemical pollutant decontamination property.
 8. Functional transitional metal silicate as claimed in claim 6, wherein cupric silicate having silicate to copper ratio of about 1:1 possessed the following properties when prepared under neutral conditions: characteristic g values of the peaks as obtained by the electron spin resonance spectrometer being (a)
 3. 1; (b)
 2. 3; (c) 2.0; (d) 1.2 and (e) 0.9; X-ray diffraction analysis having 3 significant peaks at 16.1,
 32. 2 and
 39. 7 having peak heights of 940,764 and 694 respectively; exhibiting decontamination property of metals such as arsenic, bacterial disinfecting property and antifungal property.
 9. Functional transitional metal silicate as claimed in claim 6, wherein cupric silicate having silicate to copper ratio of about 1:0. 8 possessed the following properties when prepared under acidic conditions and at70° C to 90° C.: characteristic g values of the peaks as obtained by the electron spin resonance spectrometer being (a) 2.2 and (b) 2.0; X-ray diffraction analysis having 3 significant peaks at 16, 32 and 39 having peak heights of 835 706 and502 respectively, exhibiting decontamination property of metals such as arsenic, and bacterial disinfecting property.
 10. Functional transitional metal silicate as claimed in claim 6, wherein cupric silicate having silicate to copper ratio of about 1:
 0. 8 possessed the following properties when prepared under basic conditions: characteristic g values of the peaks as obtained by the electron spin resonance spectrometer being (a) 3.7 and (b) 3.2 and (c) 2.6; X-ray diffraction analysis having 1 significant peak at 26.64 having peak height of
 152. 11. Functional transitional metal silicate as claimed in claim 6, wherein cupric silicate having silicate to copper ratio of about 1:0.53. possessed the following properties when prepared under extremely acidic conditions: characteristic g values of the peaks as obtained by the electron spin resonance spectrometer being (a) 2.1, (b) 2.0 and (c) 2.1; X-ray diffraction analysis having 3 significant peaks at 16.1, 32.2 and
 39. 71 having peak heights of 400, 394and 330 respectively; exhibiting decontamination property of metals such as arsenic and bacterial disinfecting property.
 12. Functional transitional metal silicate as claimed in claim 6, wherein cupric silicate having silicate to copper ratio of about 1:0.34 possessed the following properties when prepared under extremely acidic conditions: characteristic g values of the peaks as obtained by the electron spin resonance spectrometer being (a) 2.1, and (b) 2.0; X-ray diffraction analysis having 3 significant peaks at 16.2,
 32. 3 and
 39. 8 having peak heights of 541, 414and 365 respectively; exhibiting decontamination property of metals such as arsenic and bacterial disinfecting property.
 13. Functional transitional metal silicate as claimed in claim 3, wherein the zinc silicate has silicate to zinc ratio in the range of 1:2.46 to 1:12.13.
 14. Functional transitional metal silicate as claimed in claim 13, wherein zinc silicate having silicate to zinc ratio of about 1:12.13 possessed the following properties when prepared under neutral conditions: characteristic g values of the peaks as obtained by the electron spin resonance spectrometer being (a)5.4; (b)
 4. 5; (c) 2.5; (d) 2.1 and (e) 2.0; X-ray diffraction analysis having 3 significant peaks at
 32. 7, 59.5 and
 26. 2 having peak heights of 444,307 and 263 respectively, decontamination property of metals such as arsenic, bacterial disinfecting property and anti-bacterial property.
 15. Functional transitional metal silicate as claimed in claim 13, wherein zinc silicate having silicate to zinc ratio of about 1: 2.46 possessed the following properties when prepared under extremely acidic conditions: characteristic g values of the peaks as obtained by the electron spin resonance spectrometer being (a) 4.3; (b) 4.0; (c) 2.5; (d) 1.8 and (e) 2.0; X-ray diffraction analysis having 3 significant peaks at 11.0, 33.5 and
 32. 8 having peak heights of 2079, 835 and 664 respectively; exhibiting decontamination property of metals such as arsenic-and bacterial disinfecting property.
 16. Functional transitional metal silicate as claimed in claim 3, wherein the silver silicate has silicate to silver ratio in the range of 1:1.04 to 1:19.57.
 17. Functional transitional metal silicate as claimed in claim 16, wherein silver silicate having silicate to silver ratio of about 1:19.57 possessed the following properties when prepared under neutral conditions: characteristic g values of the peaks as obtained by the electron spin resonance spectrometer being (a) 4.3; (b) 2.3; (c) 3.9 and (d) 2.0; X-ray diffraction analysis having 3 significant peaks at 32.2, 46.2 and 27.8 having peak heights of 3945,2421 and 1835 respectively; exhibiting bacterial disinfecting property.
 18. Functional transitional metal silicate as claimed in claim 16, wherein silver silicate having silicate to silver ratio of about 1:1.04 possessed the following properties when prepared under extremely acidic conditions: characteristic g values of the peaks as obtained by the electron spin resonance spectrometer being (a) 4.3; (b) 4.0 and (c) 1.9; X-ray-diffraction analysis having 3 significant peaks at 29.3, 47.6 and 42.3 having peak heights of 2217, 684and 674 respectively; exhibiting decontamination property of metals such as arsenic and bacterial disinfecting property.
 19. Functional transitional metal silicate as claimed in claim 3, wherein the manganese silicate has silicate to manganese ratio in the range of 1:1.94 to 1:1.09.
 20. Functional transitional metal silicate as claimed in claim 19, wherein manganese silicate having silicate to manganese ratio of about 1:1.94 possessed the following properties when prepared under neutral conditions: characteristic g values of the peaks as obtained by the electron spin resonance spectrometer being (a) 1.93 and (b) 2.06; X-ray diffraction analysis having 1 significant peak at 30.6 having peak height of 148.0; exhibiting bacterial disinfecting property.
 21. Functional transitional metal silicate as claimed in claim 19, wherein manganese silicate having silicate to manganese ratio of about 1:1.09 possessed the following properties when prepared under extremely acidic conditions: characteristic g values of the peaks as obtained by the electron spin resonance spectrometer being (a) 4.3; (b) 4.1; (c) 2.1; (d) 2.1; (e) 2.0 and (f) 1.9;—X-ray diffraction analysis having I significant peak at 24.6 having peak height of 32.8; exhibiting bacterial disinfecting property.
 22. Functional transitional metal silicate as claimed in claim 3, wherein the zirconium silicate has silicate to zirconium ratio in the range of 1:2.90 to 1:0.77.
 23. Functional transitional metal silicate as claimed in claim 22, wherein zirconium silicate having silicate to zirconium ratio of about 1:2.90 possessed the following properties when prepared und decontamination property of metals such as arsenic at neutral conditions: characteristic g values of the peaks as obtained by the electron spin resonance spectrometer being (a) 4.4; (b) 4.1; (c) 2.2; (d) 2.3; (e) 2.1 and (f) 1.2; exhibiting decontamination property of metals such as arsenic.
 24. Functional transitional metal silicate as claimed in claim 22, wherein zirconium silicate having silicate to zirconium ratio of about 1:0.77 possessed the following properties when prepared under extremely acidic conditions: characteristic values of the peaks as obtained by the electron spin resonance spectrometer being (a) 4.3; (b) 2.8; (c) 1.9; (d) 1.2; (e)1.0 and (f) 0.9; X-ray diffraction analysis having 1 significant peak at 10.8 having peak height of 84.80; exhibiting and bacterial disinfecting property.
 25. Functional transitional metal silicate as claimed in claim 1, wherein the same is effective as a decontaminant of metals, chemicals, pesticides, microbes or combinations thereof.
 26. Functional transitional metal silicate as claimed in claim 1, wherein the same is effective as a disinfectant of a protozoan, a bacteria, a fungus, a virus, a microbicide or combinations thereof.
 27. Functional transitional metal silicate as claimed in claim 1, wherein the same is effective as a detoxificant of carbon monoxide, sulphur dioxide, an oxide of nitrogen, a hydrocarbon, tobacco tar, nicotine, or toxic gases or chemical conversion of toxic gases and/or toxic chemical containing gases into their non-toxic form, or combinations thereof.
 28. Functional transitional metal silicate as claimed in claim 1, wherein the same is effective as a decontaminant of trihalomethanes, proteins, semi-volatile organic compounds, volatile organic compounds, phenols, polychlorinated biphenyls and engine combustion gas.
 29. Functional transitional metal silicate as claimed in claim 26, wherein the bacteria is coliform bacteria, a Gram positive bacteria, a Gram negative bacteria or combinations thereof.
 30. Functional transitional metal silicate as claimed in claim 26, wherein the fungus is pathogenic fungi such as Sclerotium rolfsii, Rhizoctonia solani, Fusarium oxysporium, Pyricularia oryzae or combinations thereof.
 31. Functional transitional metal silicate as claimed in claim 26, wherein the virus is infective in nature.
 32. A process for preparing immobilized functional transitional metal silicates (FTMS) having transitional metal to silica ratio in the range of 0.34 to 19.57, having variable structure for same transitional metal to silica ratio, also having the variable functional structure for same transitional metal to silica ratio, exhibiting properties selected from the group comprising of decontaminant, disinfectant, protectant, microbicide or combination thereof, said process comprising the steps of: a. adding a transitional metal salt solution to a substrate to form a first product; b. adding a solution comprising a silicate to the first product to form a second product, and c. removing the non-immobilized material from the second product to form the immobilized transition metal silicate; characterized in that the amount of the transitional metal salt solution, the alkali silicate solution added are varied, temperature at which the solutions are mixed is varied between 20° to 90° C., and the pH of the medium is varied between extremely acidic condition to extremely basic condition.
 33. The process as claimed in claim 32 wherein the substrate is selected from the group consisting of agropolymers, activated alumina, aluminium oxide, cellulose, quartz sand, silica gel and combinations thereof.
 34. The process as claimed in claim 32 wherein the resins are selected from the group consisting of vinyl ester resin, a bisphenol resin, an isopthalic food grade resin and combinations thereof.
 35. Functional transitional metal silicate as claimed in claim 1, wherein the same is immobilized on materials such as activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, and functional transitional metal silicates incorporated resins and functional transition metal silicate containing resin coated sand are capable of decontaminating metals such as arsenic, mercury, etc., and this property enables immobilized functional transition metal silicates utility to purify metal contaminated drinking water, ground water and any other metal polluted aqueous streams.
 36. Functional transitional metal silicate as claimed in claim 1, wherein the same is immobilized on materials such as activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, and functional transitional metal silicates incorporated resins and functional transition metal silicate containing resin coated sand are capable of disinfecting coliform bacteria, from water and this property enables immobilized functional transition metal silicate utility to purify water free of harmful microbes.
 37. Functional transitional metal silicate as claimed in claim 1, wherein the same is immobilized on materials such as activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel, and functional transition metal silicates incorporated resins and functional transition metal silicate containing resin coated sand are capable of detoxifying toxic gases such as carbon monoxide, sulphur dioxide, nitrous oxide and hydrocarbons from combustion gases and this property enables these immobilized functional transition metal silicate containing filters usage as toxic air purifiers, chemical purifiers, chemical conversion of toxic gases and/or toxic chemical containing gases into their non-toxic form.
 38. Functional transitional metal silicate as claimed in claim 1, wherein the same is immobilized on materials such as activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel and functional transition metal silicates incorporated resins and functional transition metal silicate containing resin coated sand are capable of decontaminating pesticides such as chlorinated hydrocarbons (such as endosulphan), synthetic pyrethroides (such as cypermethrin) organophosphates (such as chloripyriphos) and this property enables these immobilized functional transition metal silicates as decontaminants of pesticides.
 39. Functional transitional metal silicate as claimed in claim 1, wherein the same is immobilized on materials such as activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel and functional transition metal silicates incorporated resins and functional transition metal silicate containing resin coated sand are capable of decontaminating proteins from an aqueous medium enabling their usage to remove or decontaminate proteins from waste waters generating from bioprocess industry, to prevent undesirable protein contamination.
 40. Functional transitional metal silicate as claimed in claim 1, wherein the same is immobilized on materials such as activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel and functional transition metal silicates incorporated resins and functional transition metal silicate containing resin coated sand are capable of decontaminating fungus from water and this property enables the usage of immobilized functional transition metal silicates for protection and or control of fungal infections.
 41. Functional transitional metal silicate as claimed in claim 1, wherein the same is immobilized on agropolymers are capable of decontaminating protozoan: (Cryptosporidium parvum) from water and this property enables the usage of immobilized functional transition metal silicates for protection and or control of protozoan infections.
 42. Functional transitional metal silicate as claimed in claim 1, wherein the same is immobilized on materials such as activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel are capable of decontaminating polio viruses, rota viruses from water and this property enables their usage of immobilized functional transition metal silicates for protection and or control of pathogenic viruses infections.
 43. Functional transitional metal silicate as claimed in claim 1, wherein the same is immobilized on materials such as activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel and functional transition metal silicates incorporated resins and functional transition metal silicate containing resin coated sand are capable of decontaminating trihalomethanes selected from the group consisting of chloroform, 1,1,1, trichloroethane, tetrachloroethylene, trichloroethylene, bromodichloroethane, dibromochloroethane, tetrachloroethylene, bromoform, 1,2, dichloro-3-bromopropane.
 44. Functional transitional metal silicate as claimed in claim 1, wherein the same is immobilized on materials such as activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel and functional transition metal silicates incorporated resins such as vinyl ester, bisphenol and isopthalic food grain resins and functional transition metal silicate containing resin coated sand are capable of decontaminating Polychlorinated biphenyls selected from the group consisting of 2,3-dichlorobiphenyl, trichlorobiphenyl, tetrachlorobiphenyl, pentachlorobiphenyl, hexachlorobiphenyl, heptachlorobiphenyl, octachlorobiphenyl.
 45. Functional transitional metal silicate as claimed in claim 1, wherein the same is immobilized on materials such as activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand silica gel and functional transition metal silicates incorporated resins such as vinyl ester, bisphenol and isopthalic food grain resins, and functional transition metal silicate containing resin coated sand are capable of decontaminating volatile organic compounds selected from the group consisting of 1,1,1, trichloroethane; 1,1,2-trichloroethane; 1,3-dichloropropane; dibromochloromethane; ethane 1,2 dibromo; chlorobenzene; benzenel, 2-dimethyl; benzene 1,3-dimethyl orthoxylene; benzenel-methylethyl; ethanel, 1,2,2-tetrachloro; bromobenzene; 2-chloro toluene; benzene, propyl; benzene, 1 chloro 4-methyl; benzene 1,2, 3-trimethyl; 4-iso propyl toluene; benzene 1.2-diethyl; benzene 1,2-dichloro; 1.3-dichlorobenzene; 1,4-dichlorobenzene; toluene; n-butylbenzene; 1 2-dibromo 3-chloropropane; 1,2,4-trichlorobenzene: naphthalene; benzene 1,2,3-trichlor, benzene 1,3,5-trichloro; benzenel, 3,4-trichloro; 1,3-butadiene 1,1,2,3, 4; benzene 2-bromo 1,3,5; nitrobenzene; styrene; benzylbenzoate; 1,2,3,4-tetramethylbenzene; benzene 1-chloro 2-propyl; 4-bromo 3-chloroanilene.
 46. Functional transitional metal silicate as claimed in claim 1, wherein the same is immobilized on materials such as activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel and functional transition metal silicates incorporated resins such as vinyl ester, bisphenol and isopthalic food grain resins, and functional transition metal silicate containing resin coated sand are capable of decontaminating semi volatile organic compounds selected from the group consisting of 1,4-dichloro; ethane hexachloro; benzene 1,2,3, trichloro; 1,3 butadiene, 1,1,2,3,4; naphthalene, 2-chloro; acenephthylene; acenapthene; phenol, 2,4-bis(1,1-imet); diethyl phthalate; fluorene; benzenel-chloro-3phenol; diphenylamine; 4-bromophenyl-phenylether; benzene, hexachloro; phenantherene; anthracene; dibutyl phthalate; fluoranthene; pyrene; benzyl butyl phthalate; chrysene; bis(2-ethylhexy)phthalate; phenol, 2,3,4,5-tetrabrom; di-n-octyl phthalate; benzo (b) fluoranthene; benzo (k) fluoranthene; benzo (a) pyrene; indeno (1,2,3-cd) pyrene; dibenzo (a, h) anthracene; benzo (g, h, l) perylene.
 47. Functional transitional metal silicate as claimed in claim 1, wherein the same is immobilized on materials such as activated alumina, aluminium oxide, agropolymers, cellulose, quartz sand, silica gel and functional transition metal silicates incorporated resins such as vinyl ester, bisphenol and isopthalic food grain resins, and functional transition metal silicates containing resin coated sand are capable of decontaminating phenols such as benzoic acid; 2,4,5-trichlorophenol; 3-nitroaniline; 3-nitrophenol; 4-nitrophenol; 2,4-dinitrophenol; 4-nitroaniline; pentachlorophenol.
 48. Functional transitional metal silicate as claimed in claim 1, wherein the same is incorporated into resins and the resin is coated on quartz sand or the quartz sand coated with functional transitional metal silicate have utility of decontamination and disinfection in high temperature zones such as boilersetc., due to thermo stability of this material.
 49. Functional transitional metal silicate as claimed in claim 1, wherein the same exhibited microbicidal nature against, bacteria, fungus and viruses enabling functional transition metal silicates usage as microbicides.
 50. Functional transitional metal silicate as claimed in claim 1, wherein the same possesses high thermal stability, decontamination and disinfection property and can be used in high temperature zones such as those existing in boilers.
 51. Functional transitional metal silicate as claimed in claim 1, wherein the same having varied metal silicate ratio exhibiting varied functions gives a method to obtain selective conjugates of transition metals along with silicates for obtaining functionally effective functional transition metal silicates to use in various other applications such as manufacturing of catalysts, and hybridizing or doping with zeolites to impart desirable properties such as anti-microbial nature etc.
 52. Functional transitional metal silicate as claimed in claim 1, wherein the same is capable of disinfecting gram positive and gram negative bacteria, fungus, and viruses enabling the usage of these novel functional transition metal silicates in detergents, deodorants, cleaning solutions, seed coat treatments, disinfectants, paints, plastics, paper, shampoos etc, for protection against microbial infections.
 53. Functional transitional metal silicate as claimed in claim 1, wherein achieving of an inclusion of a desired functionality in a selected functional transition metal silicate is attainable by optimization of synthetic conditions out of variable functions resulting from different metal silicate ratios (Examples: Inclusion of arsenic sequestration ability into silver silicate, inclusion of bacterial decontamination property into zirconium silicate, inclusion of effective bactericidal and fungicidal property into cupric silicate).
 54. Functional transitional metal silicate as claimed in claim 1, wherein achieving of an inclusion of a desired functionality in a selected functional transition metal silicate is attainable by optimization of synthetic conditions out of variable functional structures for same transitional metal to silica ratio (Example: cupric silicate having same silicate to copper ratio when prepared under acidic conditions had entirely different functional structure as compared to cupric silicate having same silicate to copper ratio and prepared under basic conditions). 